Dose dependence of nano-hardness of 6H-SiC crystal under irradiation with inert gas ions

文献类型：期刊论文

作者Song, Yin2; Yang, Yitao2; Zhang, Chonghong2; Su, Changhao1,2; Ding, Zhaonan2
刊名NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS
出版日期2018-05-01
卷号422页码:50-53
关键词6H-SiC Inert gas ions irradiation Nanoindentation Irradiation hardening
ISSN号0168-583X
DOI10.1016/j.nimb.2018.02.035
英文摘要Single crystal 6H-SiC was irradiated by inert gas ions (He, Ne, Kr and Xe ions) to various damage levels at room temperature. Nano-indentation test was performed to investigate the hardness change behavior with damage. The depth profile of nano-hardness for 6H-SiC decreased with increasing depth for both the pristine and irradiated samples, which was known as indentation size effect (ISE). Nix-Gao model was proposed to determine an asymptotic value of nano-hardness by taking account of ISE for both the pristine and irradiated samples. In this study, nano-hardness of the irradiated samples showed a strong dependence on damage level and showed a weak dependence on ions species. From the dependence of hardness on damage, it was found that the change of hardness demonstrated three distinguishable stages with damage: (I) The hardness increased with damage from 0 to 0.2 dpa and achieved a maximum of hardening fraction similar to 20% at 0.2 dpa. The increase of hardness in this damage range was contributed to defects produced by ion irradiation, which can be described well by Taylor relation. (II) The hardness reduced rapidly with large decrement in the damage range from 0.2 to 0.5 dpa, which was considered to be from the covalent bond breaking. (III) The hardness reduced with small decrement in the damage range from 0.5 to 2.2 dpa, which was induced by extension of the amorphous layer around damage peak.
WOS关键词SILICON-CARBIDE ; MECHANICAL-PROPERTIES ; NEUTRON-IRRADIATION ; HELIUM ; INDENTATION ; AMORPHIZATION ; IMPLANTATION ; CHALLENGES ; EVOLUTION ; NANOHARDNESS
资助项目National Natural Science Foundation of China (NSFC)[11475230] ; National Natural Science Foundation of China (NSFC)[91426304]
WOS研究方向Instruments & Instrumentation ; Nuclear Science & Technology ; Physics
语种英语
WOS记录号WOS:000430766100009
出版者ELSEVIER SCIENCE BV
资助机构National Natural Science Foundation of China (NSFC)
源URL[http://119.78.100.186/handle/113462/47650]  
专题近代物理研究所_能源材料研究组
近代物理研究所_材料研究中心
作者单位1.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
2.Chinese Acad Sci, Inst Modern Phys, Lanzhou 730000, Gansu, Peoples R China
推荐引用方式
GB/T 7714		 Song, Yin,Yang, Yitao,Zhang, Chonghong,et al. Dose dependence of nano-hardness of 6H-SiC crystal under irradiation with inert gas ions[J]. NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS,2018,422:50-53.
APA Song, Yin,Yang, Yitao,Zhang, Chonghong,Su, Changhao,&Ding, Zhaonan.(2018).Dose dependence of nano-hardness of 6H-SiC crystal under irradiation with inert gas ions.NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS,422,50-53.
MLA Song, Yin,et al."Dose dependence of nano-hardness of 6H-SiC crystal under irradiation with inert gas ions".NUCLEAR INSTRUMENTS & METHODS IN PHYSICS RESEARCH SECTION B-BEAM INTERACTIONS WITH MATERIALS AND ATOMS 422(2018):50-53.

入库方式： OAI收割

来源：近代物理研究所

浏览0
下载0
收藏0
其他版本

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。