Tensile fracture behavior of thermal barrier coatings on superalloy
文献类型：期刊论文
| 作者 | Z. B. Chen ; Z. G. Wang ; S. J. Zhu |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2011 |
| 卷号 | 205期号:15页码:3931-3938 |
| 关键词 | Thermal barrier coating Air plasma spraying High velocity oxygen fuel Tensile fracture Interface fracture toughness mechanical-properties interface crack tbcs |
| ISSN号 | 0257-8972 |
| 中文摘要 | Tensile fracture behavior of thermal barrier coatings (TBCs) on superalloy was investigated in air at room temperature (RT). 650 degrees C and 850 degrees C. The bond coat NiCrAlY was fabricated by either high velocity oxygen fuel (HVOF) or air plasma spraying (APS), and the top coat 7%Y(2)O(3)-ZrO(2) was deposited by APS. Thus two kinds of the TBC system were formed. It was shown that the coating had little effect on tensile stress-strain curves of the substrate and similar tensile strength was obtained in two kinds of the TBC system. However, the cracking behavior in the two kinds of TBC system at RT was different, which was also different from that at 650 degrees C and 850 degrees C by scanning electron microscopy. The interface fracture toughness of the two kinds of TBC system was evaluated by the Suo-Hutchinson model and the stress distribution in the coating and substrate was analyzed by the shear lag model. (C) 2011 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30280]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. B. Chen,Z. G. Wang,S. J. Zhu. Tensile fracture behavior of thermal barrier coatings on superalloy[J]. Surface & Coatings Technology,2011,205(15):3931-3938. |
| APA | Z. B. Chen,Z. G. Wang,&S. J. Zhu.(2011).Tensile fracture behavior of thermal barrier coatings on superalloy.Surface & Coatings Technology,205(15),3931-3938. |
| MLA | Z. B. Chen,et al."Tensile fracture behavior of thermal barrier coatings on superalloy".Surface & Coatings Technology 205.15(2011):3931-3938. |