Enhancement of ductility in high strength Mg-Gd-Y-Zr alloy
文献类型：期刊论文
| 作者 | L. Gao ; R. S. Chen ; E. H. Han |
| 刊名 | Transactions of Nonferrous Metals Society of China
 |
| 出版日期 | 2011 |
| 卷号 | 21期号:4页码:863-868 |
| 关键词 | Mg-Gd-Y alloy ductility multiaxial forging microstructure dynamic precipitate severe plastic-deformation magnesium alloy grain-refinement mechanical-properties microstructure |
| ISSN号 | 1003-6326 |
| 中文摘要 | A high strength GW94 alloy with fully recrystallized microstructure and equiaxed ultrafine grains of submicron size was produced by multiaxial forging and ageing. The alloy exhibits an ultimate tensile strength of 377 MPa, proof stress of 295 MPa and elongation to failure of 21.7%. The ductility is improved in comparison with that of the conventional extrusion processing. Superplastic ductility is achieved in tensile testing at 573 K with a maximum elongation of 450%. These high ductility and high strength are attributed to the coexistence of fully recrystallized grains and nanoscale Mg(5)(Gd, Y) particles dynamically precipitated at grain boundaries. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30341]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Gao,R. S. Chen,E. H. Han. Enhancement of ductility in high strength Mg-Gd-Y-Zr alloy[J]. Transactions of Nonferrous Metals Society of China,2011,21(4):863-868. |
| APA | L. Gao,R. S. Chen,&E. H. Han.(2011).Enhancement of ductility in high strength Mg-Gd-Y-Zr alloy.Transactions of Nonferrous Metals Society of China,21(4),863-868. |
| MLA | L. Gao,et al."Enhancement of ductility in high strength Mg-Gd-Y-Zr alloy".Transactions of Nonferrous Metals Society of China 21.4(2011):863-868. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。