Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload
文献类型：期刊论文
| 作者 | Y. Z. Jia ; J. Q. Wang ; E. H. Han ; W. Ke |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2011 |
| 卷号 | 27期号:11页码:1039-1046 |
| 关键词 | Stress corrosion cracking X80 pipeline steel Near-neutral pH solution Preload soil environment groundwater initiation behavior |
| ISSN号 | 1005-0302 |
| 中文摘要 | Constant load tests in NS4 solution purged with N(2)-5%CO(2) gas mixture were conducted on American Petroleum Institute (API) X80 pipeline steel applied in the 2nd West-East Gas Pipeline project with and without preload. The results show that cracks could initiate and propagate in X80 pipeline steel in near-neutral pH environment under a constant load condition. The life of crack initiation and propagation increased with decreasing applied stress. Preload did not change its corrosion behavior obviously. However, preload reduced the time for crack initiation. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30420]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. Z. Jia,J. Q. Wang,E. H. Han,et al. Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload[J]. Journal of Materials Science & Technology,2011,27(11):1039-1046. |
| APA | Y. Z. Jia,J. Q. Wang,E. H. Han,&W. Ke.(2011).Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload.Journal of Materials Science & Technology,27(11),1039-1046. |
| MLA | Y. Z. Jia,et al."Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload".Journal of Materials Science & Technology 27.11(2011):1039-1046. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。