Stress corrosion cracking of uni-directionally cold worked 316NG stainless steel in simulated PWR primary water with various dissolved hydrogen concentrations
文献类型：期刊论文
| 作者 | F. J. Meng ; Z. P. Lu ; T. Shoji ; J. Q. Wang ; E. H. H. Han ; W. Ke |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2011 |
| 卷号 | 53期号:8页码:2558-2565 |
| 关键词 | Stainless steel SEM Stress corrosion Hardening Potential parameters high-temperature water dependence alloys growth |
| ISSN号 | 0010-938X |
| 中文摘要 | Stress corrosion cracking growth rate of uni-directionally cold-rolled 316L stainless steel was monitored in simulated PWR primary water with different dissolved hydrogen (DH) concentrations at 320 degrees C. Crack growth rate at a DH of 0.16 cm(3) (STP) H(2)/kg H(2)O is close to that at 5 cm(3) (STP) H(2)/kg H(2)O. Crack growth rate at 30 cm(3) (STP) H(2)/kg H(2)O is about one fourth of that at 5 cm(3) (STP) H(2)/kg H(2)O or two times of that at 50 cm(3) (STP) H(2)/kg H(2)O. Electron back scattering diffraction results show typical intergranular SCC along high angle boundaries with high levels of deformation. (C) 2011 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30590]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | F. J. Meng,Z. P. Lu,T. Shoji,et al. Stress corrosion cracking of uni-directionally cold worked 316NG stainless steel in simulated PWR primary water with various dissolved hydrogen concentrations[J]. Corrosion Science,2011,53(8):2558-2565. |
| APA | F. J. Meng,Z. P. Lu,T. Shoji,J. Q. Wang,E. H. H. Han,&W. Ke.(2011).Stress corrosion cracking of uni-directionally cold worked 316NG stainless steel in simulated PWR primary water with various dissolved hydrogen concentrations.Corrosion Science,53(8),2558-2565. |
| MLA | F. J. Meng,et al."Stress corrosion cracking of uni-directionally cold worked 316NG stainless steel in simulated PWR primary water with various dissolved hydrogen concentrations".Corrosion Science 53.8(2011):2558-2565. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。