Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water
文献类型：期刊论文
| 作者 | Q. J. Peng ; H. Xue ; J. Hou ; K. Sakaguchi ; Y. Takeda ; J. Kuniya ; T. Shoji |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2011 |
| 卷号 | 53期号:12页码:4309-4317 |
| 关键词 | Low alloy steel Alloy SEM TEM Stress corrosion Welding environmentally-assisted cracking nickel-base alloys stainless-steels susceptibility property |
| ISSN号 | 0010-938X |
| 中文摘要 | Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-low alloy steel (LAS) dissimilar weld joint in 288 C water was investigated by experiments and finite element simulation. Creviced bent beam and crack growth rate (CGR) experiments showed that, while the FB was a barrier to SCC growth, further crack growth into LAS was activated by a combined effect of sulfate and dissolved oxygen in water. Finite element simulation suggested that a positive gradient of hardness as the crack approached to the FB in dilution zone caused decreased CGR. Role of microstructure and water chemistry in SCC was discussed. (C) 2011 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30619]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. J. Peng,H. Xue,J. Hou,et al. Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water[J]. Corrosion Science,2011,53(12):4309-4317. |
| APA | Q. J. Peng.,H. Xue.,J. Hou.,K. Sakaguchi.,Y. Takeda.,...&T. Shoji.(2011).Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water.Corrosion Science,53(12),4309-4317. |
| MLA | Q. J. Peng,et al."Role of water chemistry and microstructure in stress corrosion cracking in the fusion boundary region of an Alloy 182-A533B low alloy steel dissimilar weld joint in high temperature water".Corrosion Science 53.12(2011):4309-4317. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。