Failure analysis of the brass tubes in a lubricating oil cooler

文献类型:期刊论文

作者S. Qu ; G. Yao ; J. F. Tian ; Z. F. Zhang
刊名Engineering Failure Analysis
出版日期2011
卷号18期号:8页码:2232-2239
关键词Lubricating oil cooler Brass tubes Pit Dezincification Stress corrosion cracking (SCC)
ISSN号1350-6307
中文摘要Failure analysis was carried out on leaked brass tubes of a lubricating oil cooler. Direct evidences of dezincification and stress corrosion cracking (SCC) were observed by scanning electron microscope (SEM) and energy dispersive spectroscopic (EDS) analysis. It is found that there are many small pits distributed on the fracture surface and EDS analysis revealed the occurrence of dezincification in the small pits. SCC was observed on the cross-sectional plane of the fracture by SEM. Ammonia test has proved the existence of residual stress in the as-received tubes. It is determined that the brass tubes have been suffered from the coaction between dezincification and SCC. (C) 2011 Elsevier Ltd. All rights reserved.
原文出处://WOS:000297566700027
公开日期2012-04-13
源URL[http://210.72.142.130/handle/321006/30631]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
S. Qu,G. Yao,J. F. Tian,et al. Failure analysis of the brass tubes in a lubricating oil cooler[J]. Engineering Failure Analysis,2011,18(8):2232-2239.
APA S. Qu,G. Yao,J. F. Tian,&Z. F. Zhang.(2011).Failure analysis of the brass tubes in a lubricating oil cooler.Engineering Failure Analysis,18(8),2232-2239.
MLA S. Qu,et al."Failure analysis of the brass tubes in a lubricating oil cooler".Engineering Failure Analysis 18.8(2011):2232-2239.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。