Preliminary investigation on strong magnetic field treated NiAl-Cr(Mo)-Hf near eutectic alloy
文献类型：期刊论文
| 作者 | L. Y. Sheng ; J. T. Guo ; W. L. Ren ; Z. X. Zhang ; Z. M. Ren ; H. Q. Ye |
| 刊名 | Intermetallics
 |
| 出版日期 | 2011 |
| 卷号 | 19期号:2页码:143-148 |
| 关键词 | Nickel aluminides based on NiAl Mechanical properties at ambient temperature Mechanical properties at high temperatures Heat treatment Microstructure mechanical-properties nial-cr microstructure |
| ISSN号 | 0966-9795 |
| 中文摘要 | The Ni-33Al-28Cr-6Mo-0.3Hf near eutectic alloy was treated in a 10 T strong magnetic field at 1073 K and 1173 K for 1.5 h respectively. Microstructure examination reveals that after the strong magnetic field treatment, most Ni(2)AlHf Heusler particles have changed into Hf solid solution, and moreover Hf solid solution and Heusler particles along eutectic cell boundaries distribute more uniformly. In addition, the eutectic cellular microstructure of the alloy with strong magnetic field treatment at 1173 K is changed greatly. The eutectic cell has an obvious disintegration and Cr(Mo) plates become coarsening and spheroidizing. The compression tests show that room temperature compressive ductility of the alloys with strong magnetic field treatment improves significantly, compared with the heat-treated alloy. (C) 2010 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30652]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Y. Sheng,J. T. Guo,W. L. Ren,et al. Preliminary investigation on strong magnetic field treated NiAl-Cr(Mo)-Hf near eutectic alloy[J]. Intermetallics,2011,19(2):143-148. |
| APA | L. Y. Sheng,J. T. Guo,W. L. Ren,Z. X. Zhang,Z. M. Ren,&H. Q. Ye.(2011).Preliminary investigation on strong magnetic field treated NiAl-Cr(Mo)-Hf near eutectic alloy.Intermetallics,19(2),143-148. |
| MLA | L. Y. Sheng,et al."Preliminary investigation on strong magnetic field treated NiAl-Cr(Mo)-Hf near eutectic alloy".Intermetallics 19.2(2011):143-148. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。