Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H(2)S at 90 degrees C
文献类型：期刊论文
| 作者 | J. W. Tang ; Y. W. Shao ; T. Zhang ; G. Z. Meng ; F. H. Wang |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2011 |
| 卷号 | 53期号:5页码:1715-1723 |
| 关键词 | Steel Weight loss EIS SEM XRD Acid corrosion acidic chloride solutions hydrogen-sulfide aqueous-solution iron sulfides electrochemical-behavior media dissolution impedance polarization environments |
| ISSN号 | 0010-938X |
| 中文摘要 | The corrosion behavior of SAE-1020 carbon steel in H(2)S-containing solutions with different concentration of HCl at 90 degrees C was investigated by weight loss, electrochemical measurements, SEM and XRD analysis. The results showed that the corrosion rate of carbon steel increased with increasing HCl concentration. Uniform corrosion was found on the carbon steel surface in H(2)S + HCl solutions, while corrosion cavities were observed in the solution only containing H(2)S. The ratio of Faradaic process of total corrosion process increased with the increase of HCl concentration. The corrosion products were solely composed of mackinawite in the H(2)S-containing solutions with or without HCl. (c) 2011 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30700]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. W. Tang,Y. W. Shao,T. Zhang,et al. Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H(2)S at 90 degrees C[J]. Corrosion Science,2011,53(5):1715-1723. |
| APA | J. W. Tang,Y. W. Shao,T. Zhang,G. Z. Meng,&F. H. Wang.(2011).Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H(2)S at 90 degrees C.Corrosion Science,53(5),1715-1723. |
| MLA | J. W. Tang,et al."Corrosion behaviour of carbon steel in different concentrations of HCl solutions containing H(2)S at 90 degrees C".Corrosion Science 53.5(2011):1715-1723. |