Effect of porosity sealing treatments on the corrosion resistance of high-velocity oxy-fuel (HVOF)-sprayed Fe-based amorphous metallic coatings
文献类型：期刊论文
| 作者 | Y. Wang ; S. L. Jiang ; Y. G. Zheng ; W. Ke ; W. H. Sun ; J. Q. Wang |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2011 |
| 卷号 | 206期号:6页码:1307-1318 |
| 关键词 | Metallic coatings Sealing treatment Corrosion Amorphous structures Passivity matrix composites aluminum-alloy passive films protection behavior oxide surface acid al improvement |
| ISSN号 | 0257-8972 |
| 中文摘要 | High-velocity oxy-fuel-sprayed FeCrMoMnWBCSi amorphous metallic coatings were sealed with sodium orthosilicate (Na(3)SiO(4)), aluminium phosphate (AlPO(4)), and cerium salt sealants. The microstructure of the sealed coatings was characterised by scanning electron microscopy, energy dispersive spectrometer, and X-ray diffraction. Corrosion behaviour was examined using electrochemical methods of potentiodynamic polarisation, cyclic polarisation, electrochemical impedance spectroscopy, and Mott-Schottky tests. The results indicated that the uniform corrosion resistance of the three sealed coatings was enhanced greatly, and the passive current densities were decreased by one order of magnitude after the sealing treatments. The AlPO(4) sealant can penetrate the coatings by no less than 50 mu m and enhance their hardness, which exhibited a more uniform corrosion resistance, fairly good pitting corrosion resistance, and can be applied in long-term corrosive and/or abrasive environments. The cerium salt-sealed coating showed better pitting corrosion resistance but inferior corrosion resistance in the local regions of micro-cracks, which was practically used for temporary corrosion protection. The Na(3)SiO(4)-sealed coating showed better uniform corrosion resistance and inferior pitting corrosion resistance, which can be applied in short-term corrosion environments. The stability of the passive film affected the corrosion behaviour of the sealed coatings. The AlPO(4)-sealed coating performed better as a protective passive film during the long-term immersion test for a lower defect concentration and a more protective passive film. (C) 2011 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30755]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Y. Wang,S. L. Jiang,Y. G. Zheng,et al. Effect of porosity sealing treatments on the corrosion resistance of high-velocity oxy-fuel (HVOF)-sprayed Fe-based amorphous metallic coatings[J]. Surface & Coatings Technology,2011,206(6):1307-1318. |
| APA | Y. Wang,S. L. Jiang,Y. G. Zheng,W. Ke,W. H. Sun,&J. Q. Wang.(2011).Effect of porosity sealing treatments on the corrosion resistance of high-velocity oxy-fuel (HVOF)-sprayed Fe-based amorphous metallic coatings.Surface & Coatings Technology,206(6),1307-1318. |
| MLA | Y. Wang,et al."Effect of porosity sealing treatments on the corrosion resistance of high-velocity oxy-fuel (HVOF)-sprayed Fe-based amorphous metallic coatings".Surface & Coatings Technology 206.6(2011):1307-1318. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。