On the development of metallic inert anode for molten CaCl(2)-CaO System
文献类型：期刊论文
| 作者 | H. Y. Yin ; L. L. Gao ; H. Zhu ; X. H. Mao ; F. X. Gan ; D. H. Wang |
| 刊名 | Electrochimica Acta
 |
| 出版日期 | 2011 |
| 卷号 | 56期号:9页码:3296-3302 |
| 关键词 | Inert anode Anodic behavior Chloride melts Solubility of oxide cryolite-alumina melts electrochemical reduction calcium-chloride nickel ferrite cao-cacl2 melt part i electrolysis titanium solubility mechanism |
| ISSN号 | 0013-4686 |
| 中文摘要 | Some fundamental aspects related to inert anode development in molten CaCl(2)-CaO were investigated based on thermodynamic analysis, electrochemistry of metals and solubility of oxide measurements. The Gibbs free energy change of several key anodic reactions including electro-stripping of metals, electro-formation of metallic oxides, electro-dissolution of metallic oxides as well as oxygen and chlorine evolution was calculated and documented, for the first time, as a reference to develop metallic inert anode in chloride based melts. The anodic behaviors of typical metals (Ni, Fe, Co, Mo, Cu, Ag, and Pt) in the melt were investigated. The results confirmed the thermodynamic stability order of metals in the melts and revealed that surface oxide formation can increase the stability of the electrodes in CaO containing melt. Furthermore, solubility of several oxides (NiO, Fe(2)O(3), Cr(2)O(3), Co(3)O(4), NiFe(2)O(4)) in pure CaCl(2) or CaCl(2)-CaO melts was measured to evaluate the stability of oxide coating or a cermet inert anode in the melt. It was found that the solubility of NiO decreased with increasing CaO concentration, while that of Fe(2)O(3) increased. Ni coated with NiO film had much higher stability during anodic polarization. (C) 2011 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30844]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. Y. Yin,L. L. Gao,H. Zhu,et al. On the development of metallic inert anode for molten CaCl(2)-CaO System[J]. Electrochimica Acta,2011,56(9):3296-3302. |
| APA | H. Y. Yin,L. L. Gao,H. Zhu,X. H. Mao,F. X. Gan,&D. H. Wang.(2011).On the development of metallic inert anode for molten CaCl(2)-CaO System.Electrochimica Acta,56(9),3296-3302. |
| MLA | H. Y. Yin,et al."On the development of metallic inert anode for molten CaCl(2)-CaO System".Electrochimica Acta 56.9(2011):3296-3302. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。