High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900 degrees C
文献类型：期刊论文
| 作者 | P. Yu ; W. Wang ; F. H. Wang ; S. L. Zhu |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2011 |
| 卷号 | 206期号:1页码:68-74 |
| 关键词 | K38 superalloy Nanocrystalline coating Yttrium Molten sulfate High temperature corrosion oxidation behavior hot-corrosion resistance alloys scales k38g |
| ISSN号 | 0257-8972 |
| 中文摘要 | The high temperature corrosion behavior of sputtered Ni-based superalloy K38 nanocrystalline coatings with and without yttrium addition in molten sulfate (75 wt.% Na(2)SO(4) + 25 wt.% K(2)SO(4)) was investigated at 900 degrees C in air. The results indicated that nanocrystallization significantly increased the corrosion resistance through the rapid formation of a protective oxide scale. The addition of yttrium in the nanocrystalline coating furthermore improved the corrosion resistance of the coating. (C) 2011 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30855]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | P. Yu,W. Wang,F. H. Wang,et al. High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900 degrees C[J]. Surface & Coatings Technology,2011,206(1):68-74. |
| APA | P. Yu,W. Wang,F. H. Wang,&S. L. Zhu.(2011).High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900 degrees C.Surface & Coatings Technology,206(1),68-74. |
| MLA | P. Yu,et al."High-temperature corrosion behavior of sputtered K38 nanocrystalline coatings with and without yttrium addition in molten sulfate at 900 degrees C".Surface & Coatings Technology 206.1(2011):68-74. |