Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without NiCrAlYSi coating
文献类型：期刊论文
| 作者 | K. Zhang ; M. M. Liu ; S. L. Liu ; C. Sun ; F. H. Wang |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2011 |
| 卷号 | 53期号:5页码:1990-1998 |
| 关键词 | Cobalt Super-alloys Metal coatings EPMA Hot corrosion temperature oxidation behavior aluminide coatings cyclic oxidation sprayed coatings microstructure superalloys resistance yttrium |
| ISSN号 | 0010-938X |
| 中文摘要 | A NiCrAlYSi coating was deposited by arc ion plating on a cobalt-base super-alloy K40S to improve its hot corrosion resistance at 1173 K in air. The K40S suffered from accelerated corrosion and formed non-protective scale with poor adherence when its surface was beneath Na(2)SO(4) and Na(2)SO(4) containing 25 wt.% NaCl salt deposits. After the K40S was coated with NiCrAlYSi coating, a protective alpha-Al(2)O(3) scale was formed on the coating. Although the NiCrAlYSi coating changed into NiCoCrAlYSi during corrosion processes, it still possessed good corrosion resistance. In addition, the corrosion mechanisms were discussed on a basis of basic fluxing model. (C) 2011 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/30889]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. Zhang,M. M. Liu,S. L. Liu,et al. Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without NiCrAlYSi coating[J]. Corrosion Science,2011,53(5):1990-1998. |
| APA | K. Zhang,M. M. Liu,S. L. Liu,C. Sun,&F. H. Wang.(2011).Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without NiCrAlYSi coating.Corrosion Science,53(5),1990-1998. |
| MLA | K. Zhang,et al."Hot corrosion behaviour of a cobalt-base super-alloy K40S with and without NiCrAlYSi coating".Corrosion Science 53.5(2011):1990-1998. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。