Microstructure evolution and elemental diffusion of SiCp/Al-Cu-Mg composites prepared from elemental powder during hot pressing
文献类型：期刊论文
| 作者 | Q. Zhang ; B. L. Xiao ; Z. Y. Liu ; Z. Y. Ma |
| 刊名 | Journal of Materials Science
 |
| 出版日期 | 2011 |
| 卷号 | 46期号:21页码:6783-6793 |
| 关键词 | metal-matrix composites reinforced aluminum-alloy mechanical-properties solution temperature tensile properties aging behavior sic composites particulate al magnesium |
| ISSN号 | 0022-2461 |
| 中文摘要 | 15vol%SiCp/Al-Cu-Mg composites were fabricated by hot pressing method using pure elemental powders. Microstructure evolution and elemental diffusion of Cu and Mg were studied. The microstructure of as-hot pressed composites and the elemental distribution of the composites before and after solution treatment were also investigated. The results showed that there were two types of eutectic liquid phases with different compositions after the compact was heated to 580 degrees C. After the compact was held at 580 degrees C for 60 min, the eutectic liquid was absorbed into the Al matrix and some equilibrium liquid phases formed in the boundaries of the initial Al particles. Meanwhile, Cu was homogeneously distributed in the Al particles while Mg tended to be distributed near the boundaries of the initial Al particles and in the SiC clusters. The presence of Al(2)Cu, Mg(2)Si, and some oxides of Mg was identified in the as-hot pressed composite. After solution treatment, Al(2)Cu dissolved into the Al matrix, however, some Mg-rich compounds (silicide and oxide of Mg) did not dissolve into the matrix completely. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/30898]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. Zhang,B. L. Xiao,Z. Y. Liu,et al. Microstructure evolution and elemental diffusion of SiCp/Al-Cu-Mg composites prepared from elemental powder during hot pressing[J]. Journal of Materials Science,2011,46(21):6783-6793. |
| APA | Q. Zhang,B. L. Xiao,Z. Y. Liu,&Z. Y. Ma.(2011).Microstructure evolution and elemental diffusion of SiCp/Al-Cu-Mg composites prepared from elemental powder during hot pressing.Journal of Materials Science,46(21),6783-6793. |
| MLA | Q. Zhang,et al."Microstructure evolution and elemental diffusion of SiCp/Al-Cu-Mg composites prepared from elemental powder during hot pressing".Journal of Materials Science 46.21(2011):6783-6793. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。