Preparation and Corrosion Performance of PEO Coating With Low Porosity on Magnesium Alloy AZ91D In Acidic KF System
文献类型：期刊论文
| 作者 | W. Zhang ; B. Tian ; K. Q. Du ; H. X. Zhang ; F. H. Wang |
| 刊名 | International Journal of Electrochemical Science
 |
| 出版日期 | 2011 |
| 卷号 | 6期号:11页码:5228-5248 |
| 关键词 | PEO coating magnesium alloy KF based electrolyte bipolar mode corrosion behavior plasma electrolytic oxidation electrochemical impedance spectroscopy silicate-containing electrolytes microarc oxidation nacl solution mg alloy resistance films behavior aluminum |
| ISSN号 | 1452-3981 |
| 中文摘要 | A plasma electrolytic oxidation (PEO) ceramic coating F-B-A with excellent compactness was prepared on magnesium alloy AZ91D in acidic KF solution with dihydric phosphate by applying a bipolar pulse voltage. For comparison, two other coatings F-M and F-M-A were prepared in the same solution with and without addition of dihydric phosphate by applying a mono-polar pulse voltage. The composition and microstructure of the coatings were characterized by XRD, XPS and SEM. While their corrosion performance in 3.5% NaCl solution was examined by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). Results showed that the F-B-A coating was uniform and compact without fissures on surface, and its porosity was around 4.8%; while the other coatings were loose and porous with porosity around 45.6% and 27.9%, respectively. The F-B-A coating showed a bi-layered microstructure, of which the outer consisted mainly of KMgF(3) and MgF(2) with seldom MgO, whereas, the inner mainly of MgF(2), Mg(3) (PO4)(2), MgHPO(4) and little MgO. The magnesium alloy with F-B-A coating exhibited corrosion resistance about three orders higher than the sample with the F-M coating. EIS tests indicated that this bi-layered coating slowed down the penetration rate of chlorine ions and postponed the initiation of pitting corrosion on substrate. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/30918]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. Zhang,B. Tian,K. Q. Du,et al. Preparation and Corrosion Performance of PEO Coating With Low Porosity on Magnesium Alloy AZ91D In Acidic KF System[J]. International Journal of Electrochemical Science,2011,6(11):5228-5248. |
| APA | W. Zhang,B. Tian,K. Q. Du,H. X. Zhang,&F. H. Wang.(2011).Preparation and Corrosion Performance of PEO Coating With Low Porosity on Magnesium Alloy AZ91D In Acidic KF System.International Journal of Electrochemical Science,6(11),5228-5248. |
| MLA | W. Zhang,et al."Preparation and Corrosion Performance of PEO Coating With Low Porosity on Magnesium Alloy AZ91D In Acidic KF System".International Journal of Electrochemical Science 6.11(2011):5228-5248. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。