Magnetocaloric and Electrical Properties in Annealed Si-Doped Ni-Mn-In Heusler Alloy Ribbons
文献类型：期刊论文
| 作者 | X. G. Zhao ; J. L. Yang ; X. W. Wang ; C. C. Hsieh ; W. C. Chang ; W. Liu ; Z. D. Zhang |
| 刊名 | Ieee Transactions on Magnetics
 |
| 出版日期 | 2011 |
| 卷号 | 47期号:10页码:2455-2458 |
| 关键词 | Electrical properties Heusler alloys magnetocaloric properties martensitic phase |
| ISSN号 | 0018-9464 |
| 中文摘要 | The magnetocaloric and electrical properties in annealed Si-doped Ni(48)Mn(39)In(13-x)Si(x) Heusler alloy ribbons with x = 0-3 have been investigated. These ribbons crystallize in a partially ordered B2 phase structure. It was observed that both the martensitic structural transition T(M) and the Curie temperature T(C) of austenitic phase decrease with increasing Si contents. The small amount of Si in the In position modifies the peak value of positive magnetic entropy change Delta S(M) for a magnetic field change H = 50 kOe, which vary from 20.2 J . kg(-1) . K(-1) for x = 0 to 23.1 J . kg(-1) . K(-1) for x = 1, and then decrease to 10.1 J . kg(-1) . K(-1) for x = 3. Meanwhile, the magnetoresistance associated with the martensitic transformation was found to be -45% for x = 2 at T = 192 K for a magnetic field change of 50 kOe. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/30956]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. G. Zhao,J. L. Yang,X. W. Wang,et al. Magnetocaloric and Electrical Properties in Annealed Si-Doped Ni-Mn-In Heusler Alloy Ribbons[J]. Ieee Transactions on Magnetics,2011,47(10):2455-2458. |
| APA | X. G. Zhao.,J. L. Yang.,X. W. Wang.,C. C. Hsieh.,W. C. Chang.,...&Z. D. Zhang.(2011).Magnetocaloric and Electrical Properties in Annealed Si-Doped Ni-Mn-In Heusler Alloy Ribbons.Ieee Transactions on Magnetics,47(10),2455-2458. |
| MLA | X. G. Zhao,et al."Magnetocaloric and Electrical Properties in Annealed Si-Doped Ni-Mn-In Heusler Alloy Ribbons".Ieee Transactions on Magnetics 47.10(2011):2455-2458. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。