Tensile property and deformation behavior of a directionally solidified Ni-base superalloy
文献类型：期刊论文
| 作者 | Z. K. Chu ; J. J. Yu ; X. F. Sun ; H. R. Guan ; Z. Q. Hu |
| 刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
 |
| 出版日期 | 2010 |
| 卷号 | 527期号:12页码:3010-3014 |
| 关键词 | Ni-base superalloy Ductility Deformation Stacking faults single-crystals strain rate temperature stress dependence alloy |
| ISSN号 | 0921-5093 |
| 中文摘要 | Tensile behavior of directionally solidified Ni-base superalloy DZ951 was studied in the temperature range of 20-1100 degrees C. Extensive TEM investigations were performed after tensile test to fracture. The yield and tensile strengths initially decrease slightly with temperature and reach minima at around 700 degrees C. With further increase in temperature, the yield and tensile strengths increase to maxima at about 760 degrees C and then decrease sharply. In contrast to changes in strength with temperature, elongation is without significant change from 20 to 700 degrees C and then decreases to a minimum at 760 degrees C. Beyond that point an increase in elongation with respect to temperature occurs. The intermediate temperature brittleness behavior for DZ951 alloy is remarkable. The deformation microstructures could be classified in three regimes. At low temperatures, the deformation was dominated by gamma' shearing by pairs of a/2 < 1 1 0 > dislocations. At high temperatures, the deformation was dominated by gamma' by-pass. Intermediate temperatures exhibited transitional behavior. The ductility minimum at 760 degrees C is due to strain localization mainly caused by stacking faults. (C) 2010 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31050]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. K. Chu,J. J. Yu,X. F. Sun,et al. Tensile property and deformation behavior of a directionally solidified Ni-base superalloy[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2010,527(12):3010-3014. |
| APA | Z. K. Chu,J. J. Yu,X. F. Sun,H. R. Guan,&Z. Q. Hu.(2010).Tensile property and deformation behavior of a directionally solidified Ni-base superalloy.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,527(12),3010-3014. |
| MLA | Z. K. Chu,et al."Tensile property and deformation behavior of a directionally solidified Ni-base superalloy".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 527.12(2010):3010-3014. |