Pit to crack transition in X-52 pipeline steel in near neutral pH environment Part 1-formation of blunt cracks from pits under cyclic loading
文献类型：期刊论文
| 作者 | B. Y. Fang ; R. L. Eadie ; W. X. Chen ; M. Elboujdaini |
| 刊名 | Corrosion Engineering Science and Technology
 |
| 出版日期 | 2010 |
| 卷号 | 45期号:4页码:302-312 |
| 关键词 | Stress corrosion cracking Crack initiation Pit to crack transition Near neutral pH Pipeline steel Blunt crack stress-corrosion cracking anodic-dissolution hydrogen scc |
| ISSN号 | 1478-422X |
| 中文摘要 | Pipeline steel specimens that had been prepitted were cyclically loaded either in air at 0.7-7 Hz or in near neutral pH solutions sparged with 5% CO(2)/balance N(2) gas mixture at similar to 1 x 10(-4) Hz. The pit to crack transition on the radial transverse and axial transverse surfaces of typical X-52 pipeline steel was studied while varying the loading conditions and the solutions. Crack initiation in air was very difficult and took millions of cycles even under aggressive conditions. In contrast, the number of cycles required to initiate cracks in near neutral pH solutions was thousands of times smaller even under less aggressive loading. The pit geometry affected the cracking at the pits. Smaller pits were less likely to crack. If the depth to width aspect ratio was <0.5, then the pits were less likely to crack. In addition, pit to crack transition was related to the severity of the loading conditions, the solution and the microstructure. The blunt crack growth observed can be described as anodic dissolution of the plastically deformed highly stressed region at the base of the pit and the pit to crack transition can be fitted to a Weibull distribution. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31088]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | B. Y. Fang,R. L. Eadie,W. X. Chen,et al. Pit to crack transition in X-52 pipeline steel in near neutral pH environment Part 1-formation of blunt cracks from pits under cyclic loading[J]. Corrosion Engineering Science and Technology,2010,45(4):302-312. |
| APA | B. Y. Fang,R. L. Eadie,W. X. Chen,&M. Elboujdaini.(2010).Pit to crack transition in X-52 pipeline steel in near neutral pH environment Part 1-formation of blunt cracks from pits under cyclic loading.Corrosion Engineering Science and Technology,45(4),302-312. |
| MLA | B. Y. Fang,et al."Pit to crack transition in X-52 pipeline steel in near neutral pH environment Part 1-formation of blunt cracks from pits under cyclic loading".Corrosion Engineering Science and Technology 45.4(2010):302-312. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。