Anisotropic stress rupture properties of the nickel-base single crystal superalloy SRR99
文献类型：期刊论文
| 作者 | G. M. Han ; J. J. Yu ; Y. L. Sun ; X. F. Sun ; Z. Q. Hu |
| 刊名 | Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing
 |
| 出版日期 | 2010 |
| 卷号 | 527期号:21-22页码:5383-5390 |
| 关键词 | Single crystal superalloy Stress rupture Anisotropy Deformation mechanism matrix dislocations temperature creep cmsx-4 orientation mechanisms alloy |
| ISSN号 | 0921-5093 |
| 中文摘要 | The influence of orientation on the stress rupture properties of a single crystal superalloy SRR99 was investigated at temperatures of 760 and 1040 degrees C. It is found that the creep anisotropic behaviour is pronounced at the lower temperature of 760 degrees C and the stress rupture life ranks in the order [0 0 1] > [1 1 1] > [0 1 1]. Despite the anisotropy of stress rupture life is evidently reduced at the higher temperature, the [1 1 1] orientation exhibits the longest life. At 760 degrees C, EBSD (electron back scattered diffraction) was adopted to measure the lattice rotation and the deduced results indicate that the dominant slip systems are (1 1 2) {1 1 1} during stress rupture test. At 1040 degrees C, the ranking order of the stress rupture life is [1 1 1] > [0 0 1] > [0 1 1] and the single crystal close to [0 1 1] orientation still shows the poorest life. In the [0 0 1] and [1 1 1] samples, regular-gamma raft structure is formed compared with [0 1 1] samples. Further observations made by TEM investigations reveal the underlying deformation mechanisms for crystals with orientations near [0 0 1], [0 1 1] and [1 1 1] under two test conditions. (C) 2010 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31135]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | G. M. Han,J. J. Yu,Y. L. Sun,et al. Anisotropic stress rupture properties of the nickel-base single crystal superalloy SRR99[J]. Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,2010,527(21-22):5383-5390. |
| APA | G. M. Han,J. J. Yu,Y. L. Sun,X. F. Sun,&Z. Q. Hu.(2010).Anisotropic stress rupture properties of the nickel-base single crystal superalloy SRR99.Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing,527(21-22),5383-5390. |
| MLA | G. M. Han,et al."Anisotropic stress rupture properties of the nickel-base single crystal superalloy SRR99".Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 527.21-22(2010):5383-5390. |