Microstructure Formation in Al-Bi-Co Immiscible Alloys Directionally Solidified with Different Melt Superheat Temperatures
文献类型：期刊论文
| 作者 | J. He ; C. Y. Xing ; J. Z. Zhao ; L. Zhao |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2010 |
| 卷号 | 26期号:2页码:136-140 |
| 关键词 | Immiscible alloys Directional solidification Melt superheat Solidification interface monotectic aluminum-alloys composite growth system |
| ISSN号 | 1005-0302 |
| 中文摘要 | The directional solidification has been carried out for the Al-4Bi-2.5Co (wt pct) alloys with different melt superheat temperatures. The microstructure characterization and the quantitative metallographic analysis have been performed. The results indicated that the Bi-rich sphere size and cellular spacing decrease with increasing melt superheat temperature. The interaction between the advancing solidification interface and the Bi-rich spheres with different sizes was analyzed. The effect of the melt superheat treatment on microstructure evolution was discussed for the immiscible alloys. The microstructure development in ternary Al-Bi-Co alloys directionally solidified with different melt superheat temperatures was clarified. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31140]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. He,C. Y. Xing,J. Z. Zhao,et al. Microstructure Formation in Al-Bi-Co Immiscible Alloys Directionally Solidified with Different Melt Superheat Temperatures[J]. Journal of Materials Science & Technology,2010,26(2):136-140. |
| APA | J. He,C. Y. Xing,J. Z. Zhao,&L. Zhao.(2010).Microstructure Formation in Al-Bi-Co Immiscible Alloys Directionally Solidified with Different Melt Superheat Temperatures.Journal of Materials Science & Technology,26(2),136-140. |
| MLA | J. He,et al."Microstructure Formation in Al-Bi-Co Immiscible Alloys Directionally Solidified with Different Melt Superheat Temperatures".Journal of Materials Science & Technology 26.2(2010):136-140. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。