Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint
文献类型：期刊论文
| 作者 | J. A. Hou ; Q. J. Peng ; Y. Takeda ; J. Kuniya ; T. Shoji |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2010 |
| 卷号 | 52期号:12页码:3949-3954 |
| 关键词 | Stress corrosion cracking Microstructure Dissimilar weld joint Fusion boundary Type-II boundary High temperature oxygenated water high-temperature water stainless-steel metal welds susceptibility diffraction evolution |
| ISSN号 | 0010-938X |
| 中文摘要 | Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-A533B low alloy steel (LAS) dissimilar weld joint in high temperature water doped with sulfate was studied following a microstructure characterization of the FB region. The microstructure characterization suggested the type-II and type-I boundaries in the dilution zone (DZ) adjacent to the FB had lower resistance to SCC growth than the FB. Crack propagating perpendicular to the FB in the DZ was observed to be blunted by pitting at the FB, followed by the reactivation from the pitting by localized oxidation along the grain boundary in LAS. (C) 2010 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31151]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. A. Hou,Q. J. Peng,Y. Takeda,et al. Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint[J]. Corrosion Science,2010,52(12):3949-3954. |
| APA | J. A. Hou,Q. J. Peng,Y. Takeda,J. Kuniya,&T. Shoji.(2010).Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint.Corrosion Science,52(12),3949-3954. |
| MLA | J. A. Hou,et al."Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint".Corrosion Science 52.12(2010):3949-3954. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。