Oxidation Behavior of TiAl(3)/Al Composite Coating on Orthorhombic-Ti(2)AlNb Based Alloy at Different Temperatures
文献类型：期刊论文
| 作者 | L. Y. Kong ; B. Lu ; X. Y. Cui ; H. Du ; T. F. Li ; T. Y. Xiong |
| 刊名 | Journal of Thermal Spray Technology
 |
| 出版日期 | 2010 |
| 卷号 | 19期号:3页码:650-656 |
| 关键词 | cold spray high-temperature oxidation orthorhombic Ti(2)AlNb alloy TiAl(3)/Al composite coating protection |
| ISSN号 | 1059-9630 |
| 中文摘要 | This paper reports the oxidation behavior of TiAl(3)/Al composite coating deposited by cold spray. The substrate alloy was orthorhombic-Ti-22Al-26Nb (at.%). The oxidation kinetics of the coating was tested at 650, 800, and 950 A degrees C, respectively. The parabolic rate constant for the coating oxidized at 650 A degrees C was k (p) = 7.2 x 10(-2) mg center dot cm(-2)center dot h(-1/2) for the tested 1200 h. For the coating oxidized at 800 A degrees C, the oxidation kinetics could be separated into two stages with k (p) value of 39.8 x 10(-2) mg center dot cm(-2)center dot h(-1/2) for the initial 910 h and 17.7 x 10(-2) mg center dot cm(-2)center dot h(-1/2) for the stage thereafter. For the coating oxidized at 950 A degrees C, the oxidation kinetics can be separated into three stages with k (p) of 136.9 x 10(-2) mg center dot cm(-2)center dot h(-1/2) in the first 100 h, followed by 26.9 x 10(-2) mg center dot cm(-2)center dot h(-1/2) from 100 to 310 h, and 11.8 x 10(-2) mg center dot cm(-2)center dot h(-1/2) from 310 to 1098 h. XRD, SEM, and EPMA were used to study the microstructure of the coating. The results indicated that the oxidation took place throughout the entire coating instead of only at the surface. The aluminum phase in the composite coating was soon oxidized to Al(2)O(3) in all tested cases. The aluminum in TiAl(3) phase was depleted gradually and oxidized to Al(2)O(3) along with the degradation of TiAl(3) to TiAl(2) and TiAl as the temperature increased and time proceeded. AlTi(2)N was also a typical oxidation product at temperature higher than 800 A degrees C. The experimental results also indicated that the protection of the coating was attributed greatly to the interlayer formed between the coating and the substrate. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31185]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Y. Kong,B. Lu,X. Y. Cui,et al. Oxidation Behavior of TiAl(3)/Al Composite Coating on Orthorhombic-Ti(2)AlNb Based Alloy at Different Temperatures[J]. Journal of Thermal Spray Technology,2010,19(3):650-656. |
| APA | L. Y. Kong,B. Lu,X. Y. Cui,H. Du,T. F. Li,&T. Y. Xiong.(2010).Oxidation Behavior of TiAl(3)/Al Composite Coating on Orthorhombic-Ti(2)AlNb Based Alloy at Different Temperatures.Journal of Thermal Spray Technology,19(3),650-656. |
| MLA | L. Y. Kong,et al."Oxidation Behavior of TiAl(3)/Al Composite Coating on Orthorhombic-Ti(2)AlNb Based Alloy at Different Temperatures".Journal of Thermal Spray Technology 19.3(2010):650-656. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。