Oxidation resistance of TiAl(3)-Al composite coating on orthorhombic Ti(2)AlNb based alloy
文献类型：期刊论文
| 作者 | L. Y. Kong ; J. Z. Qi ; B. Lu ; R. Yang ; X. Y. Cui ; T. F. Li ; T. Y. Xiong |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2010 |
| 卷号 | 204期号:14页码:2262-2267 |
| 关键词 | Ti-22Al-26Nb TiAl(3)-Al coating Cold spray High temperature oxidation protection kinetics air |
| ISSN号 | 0257-8972 |
| 中文摘要 | The TiAl(3)-Al composite coating on orthorhombic Ti(2)AlNb based alloy was prepared by cold spray. Oxidation in air at 950 degrees C indicated that the bare alloy exhibited poor oxidation resistance due to the formation of TiO(2)/AlNbO(4) mixture and intended to scale off at the TiO(2) rich zone. A nitride layer about 2 mu m was formed under the oxide layer. The oxygen invaded deeply into the alloy and caused severe microhardness enhancement in the near Surface region. The TiAl(3)-Al composite coating exhibited Parabolic oxidation kinetics and showed no sign of degradation after oxidized up to 1098 h at 950 degrees C in air under quasi-isothermal condition. No scaling of the coating was observed after oxidized at 950 degrees C up to the tested 150 cycles. The major oxide in the oxidized coating was Al(2)O(3). The AlTi(2)N, TiAl and small amount of TiO(2) were also observed in the oxidized coating. The EPMA and microhardness tests showed that inward oxygen diffusion was prevented by the interlayer, which was formed between the composite coating and the substrate during heat-treatment. Microstructure analyses demonstrated that the interlayer play a major role in protecting the substrate alloy from high temperature oxidation and interstitial embrittlement. (C) 2009 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31186]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Y. Kong,J. Z. Qi,B. Lu,et al. Oxidation resistance of TiAl(3)-Al composite coating on orthorhombic Ti(2)AlNb based alloy[J]. Surface & Coatings Technology,2010,204(14):2262-2267. |
| APA | L. Y. Kong.,J. Z. Qi.,B. Lu.,R. Yang.,X. Y. Cui.,...&T. Y. Xiong.(2010).Oxidation resistance of TiAl(3)-Al composite coating on orthorhombic Ti(2)AlNb based alloy.Surface & Coatings Technology,204(14),2262-2267. |
| MLA | L. Y. Kong,et al."Oxidation resistance of TiAl(3)-Al composite coating on orthorhombic Ti(2)AlNb based alloy".Surface & Coatings Technology 204.14(2010):2262-2267. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。