Microstructural characteristics and degradation mechanism of the NiCrAlY/CrN/DSM11 system during thermal exposure at 1100 degrees C
文献类型：期刊论文
| 作者 | W. Z. Li ; Y. Q. Li ; C. Sun ; Z. L. Hu ; T. Q. Liang ; W. Q. Lai |
| 刊名 | Journal of Alloys and Compounds
 |
| 出版日期 | 2010 |
| 卷号 | 506期号:1页码:77-84 |
| 关键词 | Coatings Diffusion barrier Interdiffusion Oxidation-resistance Microstructure temperature oxidation behavior barrier coatings diffusion barrier nicocraly coatings o-n interdiffusion superalloy interlayer design scale |
| ISSN号 | 0925-8388 |
| 中文摘要 | To limit the elemental interdiffusion, a CrN diffusion barrier was introduced into the interface of NiCrAlY overlayer and DSM11 substrate. During vacuum heat treatment and thermal exposure, the single and continuous CrN barrier layer was first changed to the multilayer structure and then to the Ti-rich interlayer. With the gradual loss of continuity in the diffusion barrier, the elemental interdiffusion was accelerated. Due to the interdiffusion, the transformation of beta-NiAl -> gamma'-Ni(3)Al -> gamma-Ni and the low Al level occurred in the overlayer. The phase transformation of metastable theta-Al(2)O(3) to stable a and the accelerated elemental interdiffusion affected the integrity of the surface scales. After 100 h exposure at 1100 degrees C, the Al element was insufficient and the duplex coatings were degraded. (c) 2010 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31239]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. Z. Li,Y. Q. Li,C. Sun,et al. Microstructural characteristics and degradation mechanism of the NiCrAlY/CrN/DSM11 system during thermal exposure at 1100 degrees C[J]. Journal of Alloys and Compounds,2010,506(1):77-84. |
| APA | W. Z. Li,Y. Q. Li,C. Sun,Z. L. Hu,T. Q. Liang,&W. Q. Lai.(2010).Microstructural characteristics and degradation mechanism of the NiCrAlY/CrN/DSM11 system during thermal exposure at 1100 degrees C.Journal of Alloys and Compounds,506(1),77-84. |
| MLA | W. Z. Li,et al."Microstructural characteristics and degradation mechanism of the NiCrAlY/CrN/DSM11 system during thermal exposure at 1100 degrees C".Journal of Alloys and Compounds 506.1(2010):77-84. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。