Anisotropic 3D growth of corrosion pits initiated at MnS inclusions for A537 steel during corrosion fatigue
文献类型：期刊论文
| 作者 | J. Ma ; B. Zhang ; J. Q. Wang ; G. Z. Wang ; E. H. Han ; W. Ke |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2010 |
| 卷号 | 52期号:9页码:2867-2877 |
| 关键词 | Steel SEM Corrosion fatigue Pitting corrosion transient dissolution behavior low-carbon steel pitting corrosion stainless-steel crack initiation mechanochemical behavior aluminum-alloy stress strain transition |
| ISSN号 | 0010-938X |
| 中文摘要 | The 3D growth behaviour of pits initiated at MnS inclusions for A537 steel under cyclic load condition has been investigated by confocal scanning laser microscope and finite element analysis. The results indicated the growth of pit for cyclic-stressed samples showed anisotropic behaviour. Significant higher growth rate was found in the direction perpendicular to load axis. Finite element analysis indicated that localized plastic strain played an important role on pit growth. The growth kinetics of pit in width direction is dominated by plastic deformation. Coalescences of pits further increase the growth rate of pit as predicted by finite element analysis. (C) 2010 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31363]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Ma,B. Zhang,J. Q. Wang,et al. Anisotropic 3D growth of corrosion pits initiated at MnS inclusions for A537 steel during corrosion fatigue[J]. Corrosion Science,2010,52(9):2867-2877. |
| APA | J. Ma,B. Zhang,J. Q. Wang,G. Z. Wang,E. H. Han,&W. Ke.(2010).Anisotropic 3D growth of corrosion pits initiated at MnS inclusions for A537 steel during corrosion fatigue.Corrosion Science,52(9),2867-2877. |
| MLA | J. Ma,et al."Anisotropic 3D growth of corrosion pits initiated at MnS inclusions for A537 steel during corrosion fatigue".Corrosion Science 52.9(2010):2867-2877. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。