HIGH-CYCLE FATIGUE BEHAVIOR OF AM3 NICKEL-BASE SINGLE CRYSTAL SUPERALLOY AT HIGH TEMPERATURE
文献类型：期刊论文
| 作者 | L. Shui ; T. Jin ; X. F. Sun ; Z. Q. Hu |
| 刊名 | International Journal of Modern Physics B
 |
| 出版日期 | 2010 |
| 卷号 | 24期号:15-16页码:2886-2891 |
| 关键词 | Nickel-base single crystal superalloy high cycle fatigue fracture microstructure creep dislocations tms-138 |
| ISSN号 | 0217-9792 |
| 中文摘要 | A single crystal nickel-base superalloy with < 001 > orientation was subjected to high cycle fatigue loading at temperature of 700 degrees C and 870 degrees C. The tests were performed in ambient atmosphere under load control at a stress ratio R=sigma(min)/sigma(max)=0.1 and a frequency of 83.3 Hz on smooth specimens. In this paper, the premature initiation and rapid propagation of cracks to failure due to high frequency cyclic loading were explored. The dislocation characteristics and fracture surface observation were evaluated through scanning electron microscopy and transmission electron microscopy, respectively. The results showed that the fatigue strength at 700 degrees C was higher than that at 870 degrees C. At 700 degrees C the interaction of cyclic stress with high temperature induced the precipitation of homogeneous hyperfine secondary gamma' particles, that is beneficial to fatigue strength. At 870 degrees C, the cyclic stress led to the formation of persistent slip bands moving through the gamma matrix channels and the gamma' precipitates. The morphology change of gamma' phase was not notable during the deformation at high frequency cyclic loading. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/31440]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Shui,T. Jin,X. F. Sun,et al. HIGH-CYCLE FATIGUE BEHAVIOR OF AM3 NICKEL-BASE SINGLE CRYSTAL SUPERALLOY AT HIGH TEMPERATURE[J]. International Journal of Modern Physics B,2010,24(15-16):2886-2891. |
| APA | L. Shui,T. Jin,X. F. Sun,&Z. Q. Hu.(2010).HIGH-CYCLE FATIGUE BEHAVIOR OF AM3 NICKEL-BASE SINGLE CRYSTAL SUPERALLOY AT HIGH TEMPERATURE.International Journal of Modern Physics B,24(15-16),2886-2891. |
| MLA | L. Shui,et al."HIGH-CYCLE FATIGUE BEHAVIOR OF AM3 NICKEL-BASE SINGLE CRYSTAL SUPERALLOY AT HIGH TEMPERATURE".International Journal of Modern Physics B 24.15-16(2010):2886-2891. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。