IrO(2)-SiO(2) binary oxide films: Preparation, physiochemical characterization and their electrochemical properties
文献类型：期刊论文
| 作者 | X. M. Wang ; J. M. Hu ; J. Q. Zhang |
| 刊名 | Electrochimica Acta
 |
| 出版日期 | 2010 |
| 卷号 | 55期号:15页码:4587-4593 |
| 关键词 | IrO(2) SiO(2) Binary oxide Electrocatalyst Oxygen evolution reaction (OER) x-ray-diffraction surface characterization oxygen evolution thin-films electrodes titanium electrocatalysts iridium anodes acid |
| ISSN号 | 0013-4686 |
| 中文摘要 | Mixed IrO(2)-SiO(2) oxide films were prepared on titanium substrate by the thermo-decomposition of hexachloroiridate (H(2)IrCl(6)) and tetraethoxysilane (TEOS) mixed precursors in organic solvents. The solution chemistry and thermal decomposition kinetics of the mixed precursors were investigated by ultra violet/visible (UV/vis) spectroscopy and thermogravimetry (TGA) and differential thermal analysis (DTA). respectively The physiochemical characterization of the resulting materials was conducted by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical measurements. It is shown from the UV/vis spectra that the electronic absorption intensity of IrCl(6)(2-) complexes in the precursors decreases in the presence of TEOS. indicating the interaction between these two components. Thermal analysis shows the decomposition reaction of H(2)IrCl(6) is inhibited by TEOS in the low temperature range, but the further oxidation reaction at high temperatures of formed intermediates is independent of the presence of silane component. Physical measurements show a restriction effect of silica on the ciystallization and crystal growth processes of IrO(2), leading to the formation of finer oxide pal tidies and the porous morphology of the binary oxide films. The porous composite films exhibit high apparent electrocatalytic activity toward the oxygen evolution reaction In addition, the long-term stability of Ti-supported IrO(2) electrodes is found to apparently improve with appropriate amount of SiO(2) incorporation, as tested under galvanostatic electrolysis. (C) 2010 Elsevier Ltd. All rights reserved |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31529]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. M. Wang,J. M. Hu,J. Q. Zhang. IrO(2)-SiO(2) binary oxide films: Preparation, physiochemical characterization and their electrochemical properties[J]. Electrochimica Acta,2010,55(15):4587-4593. |
| APA | X. M. Wang,J. M. Hu,&J. Q. Zhang.(2010).IrO(2)-SiO(2) binary oxide films: Preparation, physiochemical characterization and their electrochemical properties.Electrochimica Acta,55(15),4587-4593. |
| MLA | X. M. Wang,et al."IrO(2)-SiO(2) binary oxide films: Preparation, physiochemical characterization and their electrochemical properties".Electrochimica Acta 55.15(2010):4587-4593. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。