Effect of Different Curing Agents on Cure Reaction and Exposure Resistance of Phenolic-Epoxy Resins in Hot Acid Solutions
文献类型：期刊论文
| 作者 | Z. Wang ; E. Han ; F. Liu ; W. Ke |
| 刊名 | Corrosion
 |
| 出版日期 | 2010 |
| 卷号 | 66期号:7 |
| 关键词 | corrosion resistance curing reaction glass transition temperature phenolic-epoxy/diaminodiphenyl sulfone scanning calorimetry novolac resin corrosion coatings kinetics water temperature benzoxazine performance parameters |
| ISSN号 | 0010-9312 |
| 中文摘要 | Linear phenolic-epoxy polymers were cured with diaminodiphenyl sulfone (DDS), metaphenylene diamine (m-DPA), and phenolic aldehyde amine (PAA), respectively, to prepare several anti-corrosion materials that are coating components. The effect of different curing agents on energy of activation (E(alpha)) and glass transition temperature (T) of polymers was investigated using differential scanning calorimetry (DSC). E(alpha) of phenolic-epoxy/DDS is higher than that of phenolic-epoxy/PAA, and lower than that of phenolic-epoxy/m-DPA. The three anti-corrosion materials were immersed in 10% sulfuric acid (H(2)SO(4)) solution at 80 degrees C for 800 h. T(g) of phenolic-epoxy/DDS material varies very little before and after acid immersion testing. while T(g) of phenolic-epoxy/PAA material drastically decreases after the acid immersion test. A gravimetric liquid sorption experiment indicates that weight loss of phenolic-epoxy/DDS material is the smallest among three anti-corrosion materials. X-ray photoelectron spectroscopy (XPS) analysis demonstrates that the carbon-to-oxygen (C/O) ratio of phenolic-epoxy/DDS material after exposure testing is higher than that of phenolic-epoxy/m-DPA material and phenolic-epoxy/PAA material. The high T(g), high C/O ratio, and low weight loss of phenolic-epoxy/DDS material as a coating component during exposure are connected directly with the strong corrosion resistance of the coating. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31553]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. Wang,E. Han,F. Liu,et al. Effect of Different Curing Agents on Cure Reaction and Exposure Resistance of Phenolic-Epoxy Resins in Hot Acid Solutions[J]. Corrosion,2010,66(7). |
| APA | Z. Wang,E. Han,F. Liu,&W. Ke.(2010).Effect of Different Curing Agents on Cure Reaction and Exposure Resistance of Phenolic-Epoxy Resins in Hot Acid Solutions.Corrosion,66(7). |
| MLA | Z. Wang,et al."Effect of Different Curing Agents on Cure Reaction and Exposure Resistance of Phenolic-Epoxy Resins in Hot Acid Solutions".Corrosion 66.7(2010). |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。