Fatigue behavior of (graded) (Ti, Al)N-coated 1Cr11Ni2W2MoV stainless steel at high temperature
文献类型：期刊论文
| 作者 | L. Xin ; P. Liu ; C. J. Feng ; S. L. Zhu ; F. H. Wang |
| 刊名 | Surface & Coatings Technology
 |
| 出版日期 | 2010 |
| 卷号 | 204期号:15页码:2417-2423 |
| ISSN号 | 0257-8972 |
| 关键词 | (Graded) (Ti Al)N coating Arc ion plating High-cycle fatigue High temperature Stainless steel mechanical-properties residual-stress ceramic coatings pvd alloy microstructure resistance deposits zrn ti |
| 中文摘要 | The high-cycle fatigue properties of graded (Ti, Al)N- and Ti(0.7)Al(0.3)N-coated 1Cr11Ni2W2MoV at 500 degrees C have been investigated using a rotating bending fatigue testing machine. The results show that fatigue strength and life of 1Cr11Ni2W2MoV stainless steel were apparently increased by the presence of Ti(0.7)Al(0.3)N coating. The fatigue life and strength was also improved to some extent by the presence of the graded coating at higher stress levels (475 MPa-525 MPa). The fracture morphologies were analyzed by SEM. It is concluded that the presence of the coatings, which were well adhered and have high compressive stress, restricted plastic deformation of the substrate, thus improved the fatigue properties of the steel. (C) 2010 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31604]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Xin,P. Liu,C. J. Feng,et al. Fatigue behavior of (graded) (Ti, Al)N-coated 1Cr11Ni2W2MoV stainless steel at high temperature[J]. Surface & Coatings Technology,2010,204(15):2417-2423. |
| APA | L. Xin,P. Liu,C. J. Feng,S. L. Zhu,&F. H. Wang.(2010).Fatigue behavior of (graded) (Ti, Al)N-coated 1Cr11Ni2W2MoV stainless steel at high temperature.Surface & Coatings Technology,204(15),2417-2423. |
| MLA | L. Xin,et al."Fatigue behavior of (graded) (Ti, Al)N-coated 1Cr11Ni2W2MoV stainless steel at high temperature".Surface & Coatings Technology 204.15(2010):2417-2423. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。