Microstructures and mechanical properties of cold rolled Mg-8Li and Mg-8Li-2Al-2RE alloys
文献类型:期刊论文
作者 | H. Yan ; R. S. Chen ; E. H. Han |
刊名 | Transactions of Nonferrous Metals Society of China
![]() |
出版日期 | 2010 |
卷号 | 20页码:S550-S554 |
关键词 | magnesium alloys lithium microstructure texture Mg-Li alloy mg-li alloys |
ISSN号 | 1003-6326 |
中文摘要 | The microstructures and mechanical properties of Mg-8Li and Mg-8Li-2Al-2RE alloy sheets were evaluated after cold rolling. Both alloys contain alpha-phase and beta-phase which consists of a solid solution of Mg in BCC Li. The proportion of beta-phase in both alloys is approximately 60%. The alpha-phase and beta-phase are elongated approximately parallel to the rolling direction and there is no sign of recrystallization even after being annealed at 200 degrees C for 1 h. The yield strength of Mg-8Li-2Al-2RE sheets is about 165 MPa with elongation of 35% along rolling direction, while the yield strength is about 187 MPa with elongation of 21% along the direction titled 45 degrees to rolling direction. The alpha-phase in both alloys exhibits basal texture, and the intensity of basal texture in Mg-8Li is larger than that in Mg-8Li-2Al-2RE. However, the beta-phase shows (100) texture, and the intensity of (100) texture in Mg-8Li is twice of that in Mg-8Li-2Al-2RE. It could be attributed to the existence of RE-containing particles in Mg-8Li-2Al-2RE. |
原文出处 | |
公开日期 | 2012-04-13 |
源URL | [http://210.72.142.130/handle/321006/31620] ![]() |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | H. Yan,R. S. Chen,E. H. Han. Microstructures and mechanical properties of cold rolled Mg-8Li and Mg-8Li-2Al-2RE alloys[J]. Transactions of Nonferrous Metals Society of China,2010,20:S550-S554. |
APA | H. Yan,R. S. Chen,&E. H. Han.(2010).Microstructures and mechanical properties of cold rolled Mg-8Li and Mg-8Li-2Al-2RE alloys.Transactions of Nonferrous Metals Society of China,20,S550-S554. |
MLA | H. Yan,et al."Microstructures and mechanical properties of cold rolled Mg-8Li and Mg-8Li-2Al-2RE alloys".Transactions of Nonferrous Metals Society of China 20(2010):S550-S554. |
入库方式: OAI收割
来源:金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。