Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging
文献类型：期刊论文
| 作者 | J. Chen ; M. R. Ai ; J. Q. Wang ; E. H. Han ; W. Ke |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2009 |
| 卷号 | 51期号:5页码:1197-1200 |
| 关键词 | Magnesium Galvanostatic stress-corrosion cracking in-situ observation mg-al alloy sodium-sulfate solution wet-dry conditions na2so4 solution behavior initiation hydride steels |
| ISSN号 | 0010-938X |
| 中文摘要 | The process of hydrogen blister formation on as-cast AZ91 magnesium alloy was investigated in 0.1 M NaOH solution using galvanostatic test. The results showed that cathodic charging of AZ91 alloy resulted in hydrogen blister formation, and blister rupture caused the nucleation and propagation of transgranular micro-cracks around the ruptured blister. (C) 2009 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31824]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. Chen,M. R. Ai,J. Q. Wang,et al. Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging[J]. Corrosion Science,2009,51(5):1197-1200. |
| APA | J. Chen,M. R. Ai,J. Q. Wang,E. H. Han,&W. Ke.(2009).Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging.Corrosion Science,51(5),1197-1200. |
| MLA | J. Chen,et al."Formation of hydrogen blister on AZ91 magnesium alloy during cathodic charging".Corrosion Science 51.5(2009):1197-1200. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。