Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating
文献类型：期刊论文
| 作者 | K. F. Chen ; Y. T. Tian ; Z. Lu ; N. Ai ; X. Q. Huang ; W. H. Su |
| 刊名 | Journal of Power Sources
 |
| 出版日期 | 2009 |
| 卷号 | 186期号:1页码:128-132 |
| 关键词 | 3YSZ Electrolyte film Slurry spin coating SOFC oxide fuel-cells ysz electrolyte thin-films it-sofc fabrication temperature performance membranes ceramics nio/ysz |
| ISSN号 | 0378-7753 |
| 中文摘要 | A dense and uniform 3 mol% yttria-stabilized tetragonal zirconia polycrystal (3YSZ) electrolyte film of 6 mu m in thickness was fabricated by slurry spin coating on a porous NiO/3YSZanode substrate. Composite cathodes of La(0.7)Sr(0.3)MnO(3) impregnated with Sm(0.2)Ce(0.8)O(1.9) were fabricated on the 3YSZ films. A single cell produced in this way was tested at 700, 750 and 800 degrees C with hydrogen as fuel and stationary air as oxidant. Test results revealed an open-circuit voltage of 1.04V at 800 degrees C, and maximum power density of 551.895 and 1143 mW cm(-2) at 700,750 and 800 degrees C, respectively. Impedance spectra results demonstrated that the cell performance was determined by the polarization resistance of the cathode. (c) 2008 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/31827]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. F. Chen,Y. T. Tian,Z. Lu,et al. Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating[J]. Journal of Power Sources,2009,186(1):128-132. |
| APA | K. F. Chen,Y. T. Tian,Z. Lu,N. Ai,X. Q. Huang,&W. H. Su.(2009).Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating.Journal of Power Sources,186(1),128-132. |
| MLA | K. F. Chen,et al."Behavior of 3 mol% yttria-stabilized tetragonal zirconia polycrystal film prepared by slurry spin coating".Journal of Power Sources 186.1(2009):128-132. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。