Improved biological performance of low modulus Ti-24Nb-4Zr-7.9Sn implants due to surface modification by anodic oxidation

文献类型:期刊论文

作者Y. Gao ; B. Gao ; R. Wang ; J. Wu ; L. J. Zhang ; Y. L. Hao ; X. J. Tao
刊名Applied Surface Science
出版日期2009
卷号255期号:9页码:5009-5015
关键词Titanium alloy Anodic oxidation Biocompatibility Osteoblast Osseointegration in-vitro titanium surfaces bone response osteoblast calcium behavior alloy topography adsorption attachment
ISSN号0169-4332
中文摘要Dental implants are usually made from commercially pure titanium or titanium alloys. The purpose of this study was to evaluate the influence of surface treatment to low modulus Ti-24Nb-4Zr-7.9Sn (TNZS) on cell and bone responses. The TNZS alloy samples were modified using anodic oxidation (AD). Surface oxide properties were characterized by using various surface analytic techniques, involving scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS), X-ray diffractometry (XRD) and surface profilometer. During the AD treatment, porous titanium oxide layer was formed and Ca ions were incorporated into the oxide layer. The viability and morphology of osteoblasts on Ca-incorporated TNZS were studied. The bone responses of Ca-incorporated TNZS were evaluated by pull-out tests and morphological analysis after implantation in rabbit tibiae. The non-treated Ti and TNZS samples were used as the control. Significant increases in cell viability and pull-out forces (p < 0.05) were observed for Ca-incorporated TNZS implants compared with those for the control groups. Porous structures supplied positive guidance cues for osteoblasts to attach. The enhanced cell and bone responses to Ca-incorporated TNZS implants could be explained by the surface chemistry and microtopography. (c) 2009 Elsevier B.V. All rights reserved.
原文出处://WOS:000263542700056
公开日期2012-04-13
源URL[http://210.72.142.130/handle/321006/31929]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Y. Gao,B. Gao,R. Wang,et al. Improved biological performance of low modulus Ti-24Nb-4Zr-7.9Sn implants due to surface modification by anodic oxidation[J]. Applied Surface Science,2009,255(9):5009-5015.
APA Y. Gao.,B. Gao.,R. Wang.,J. Wu.,L. J. Zhang.,...&X. J. Tao.(2009).Improved biological performance of low modulus Ti-24Nb-4Zr-7.9Sn implants due to surface modification by anodic oxidation.Applied Surface Science,255(9),5009-5015.
MLA Y. Gao,et al."Improved biological performance of low modulus Ti-24Nb-4Zr-7.9Sn implants due to surface modification by anodic oxidation".Applied Surface Science 255.9(2009):5009-5015.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。