Effects of scratching on corrosion and stress corrosion cracking of Alloy 690TT at 58 degrees C and 330 degrees C
文献类型：期刊论文
| 作者 | F. J. Meng ; J. Q. Wang ; E. H. Han ; W. Ke |
| 刊名 | Corrosion Science
 |
| 出版日期 | 2009 |
| 卷号 | 51期号:11页码:2761-2769 |
| ISSN号 | 0010-938X |
| 关键词 | Nickel Polarization Stress corrosion tribological contact analysis hard coated surface stainless-steel repassivation kinetics localized corrosion mechanical analysis part i water deformation strain |
| 中文摘要 | Scratched Alloy 690TT were characterized using X-ray stress analysis technique, nano-indentation, SEM, electrochemical and immersion tests. The stresses adjacent to the scratches, which resulted from scratching, were tensile parallel to the scratches and compressive perpendicular to the scratches. In the acidic sodium chloride solution at 58 degrees C, scratching caused E(corr) to shift negatively owing to a transient anodic current accompanied by a larger difference between E(corr) and the potential of zero charge. Pit 330 degrees C in the lead-containing caustic solutions, SCC initiated at the scratch-banks and scratch-beds after 30 days' immersion. Scratched Alloy 69017 exhibited both IGSCC and TGSCC in initiation. (C) 2009 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32202]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | F. J. Meng,J. Q. Wang,E. H. Han,et al. Effects of scratching on corrosion and stress corrosion cracking of Alloy 690TT at 58 degrees C and 330 degrees C[J]. Corrosion Science,2009,51(11):2761-2769. |
| APA | F. J. Meng,J. Q. Wang,E. H. Han,&W. Ke.(2009).Effects of scratching on corrosion and stress corrosion cracking of Alloy 690TT at 58 degrees C and 330 degrees C.Corrosion Science,51(11),2761-2769. |
| MLA | F. J. Meng,et al."Effects of scratching on corrosion and stress corrosion cracking of Alloy 690TT at 58 degrees C and 330 degrees C".Corrosion Science 51.11(2009):2761-2769. |