Influence of Iron Microstructure on Corrosion Inhibitor Performance in Acidic Media

文献类型:期刊论文

作者E. E. Oguzie ; S. G. Wang ; Y. Li ; F. H. Wang
刊名Journal of Physical Chemistry C
出版日期2009
卷号113期号:19页码:8420-8429
关键词nanocrystalline ingot iron universal force-field mild-steel corrosion sulfuric-acid electrochemical corrosion sulfate-solution behavior thiourea derivatives molecules
ISSN号1932-7447
中文摘要Electrochemical measurements employing ac and dc techniques as well as atomic force microscopy were used to study the electrochemical corrosion behavior of ingot iron with two different microstructures: conventional polycrystalline ingot iron (CPII) and bulk nanocrystalline ingot iron (BNII) fabricated from CPII by severe rolling, without and with inhibitors. The corrosive media was 0.1 M H(2)SO(4) solution, while thiourea (TU) was employed as inhibitor, with a concentration of 5.0 mM, as well as a 1:1 combination of TU and KI. Impedance and polarization results show that BNII was more susceptible to corrosion in the uninhibited acid. The presence of TU improved the corrosion resistance of both specimens comparably, while KI reduced the inhibition efficiency of TU. Infrared spectrophotometry revealed that the interfacial species for CPII and BNII in the presence of TU were quite identical and markedly different from that in TU + KI. Molecular dynamics (MD) simulations were performed to illustrate the adsorption process of TU at a molecular level, and the theoretical predictions showed good agreement with the electrochemical results.
原文出处://WOS:000265895500064
公开日期2012-04-13
源URL[http://210.72.142.130/handle/321006/32221]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
E. E. Oguzie,S. G. Wang,Y. Li,et al. Influence of Iron Microstructure on Corrosion Inhibitor Performance in Acidic Media[J]. Journal of Physical Chemistry C,2009,113(19):8420-8429.
APA E. E. Oguzie,S. G. Wang,Y. Li,&F. H. Wang.(2009).Influence of Iron Microstructure on Corrosion Inhibitor Performance in Acidic Media.Journal of Physical Chemistry C,113(19),8420-8429.
MLA E. E. Oguzie,et al."Influence of Iron Microstructure on Corrosion Inhibitor Performance in Acidic Media".Journal of Physical Chemistry C 113.19(2009):8420-8429.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。