Electrochemical behaviour of high nitrogen bearing stainless steel in acidic chloride solution: Effects of oxygen, acid concentration and surface roughness

文献类型:期刊论文

作者Y. X. Qiao ; Y. G. Zheng ; P. C. Okafor ; W. Ke
刊名Electrochimica Acta
出版日期2009
卷号54期号:8页码:2298-2304
关键词Corrosion Stainless steel Corrosion potentials Acid Oxygen Surface roughness pitting corrosion passive films reduction chromium dissolution electrodes hydrogen iron
ISSN号0013-4686
中文摘要The effects of oxygen, H(2)SO(4) concentration and surface roughness on the electrochemical behaviour of high nitrogen bearing stainless steel (HNS) in acidified 0.5 M NaCl solution were investigated using potentiodynamic polarization method. The results revealed three corrosion potentials indicating an unstable system. The number of the potentials was influenced by H(2)SO(4) concentration. Three potentials existed above 0.011 M H(2)SO(4), two between 0.011 and 0.0065 M H(2)SO(4) and one below 0.0065 M H(2)SO(4). Oxygen increased the number of corrosion potential at 0.005 M H(2)SO(4) + 0.5 M NaCl solution while surface roughness had no noticeable influence on the number of potentials but increased the values of the corrosion potentials and passivation current densities with increase in the surface roughness. The corrosion mechanism has been discussed using the ideal polarization curve models. (C) 2008 Elsevier Ltd. All rights reserved.
原文出处://WOS:000264303100024
公开日期2012-04-13
源URL[http://210.72.142.130/handle/321006/32240]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
Y. X. Qiao,Y. G. Zheng,P. C. Okafor,et al. Electrochemical behaviour of high nitrogen bearing stainless steel in acidic chloride solution: Effects of oxygen, acid concentration and surface roughness[J]. Electrochimica Acta,2009,54(8):2298-2304.
APA Y. X. Qiao,Y. G. Zheng,P. C. Okafor,&W. Ke.(2009).Electrochemical behaviour of high nitrogen bearing stainless steel in acidic chloride solution: Effects of oxygen, acid concentration and surface roughness.Electrochimica Acta,54(8),2298-2304.
MLA Y. X. Qiao,et al."Electrochemical behaviour of high nitrogen bearing stainless steel in acidic chloride solution: Effects of oxygen, acid concentration and surface roughness".Electrochimica Acta 54.8(2009):2298-2304.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。