Partial recrystallization in the nugget zone of friction stir welded dual-phase Cu-Zn alloy
文献类型：期刊论文
| 作者 | G. M. Xie ; Z. Y. Ma ; L. Geng |
| 刊名 | Philosophical Magazine
 |
| 出版日期 | 2009 |
| 卷号 | 89期号:18页码:1505-1516 |
| 关键词 | friction stir welding copper alloy recrystallization electron backscatter diffraction mechanical-properties aluminum-alloys brass plates texture microstructures microtexture parameters copper flow |
| ISSN号 | 1478-6435 |
| 中文摘要 | For single and quasi-single phase metallic materials, complete dynamic recrystallization has been observed in the nugget zones (NZs) of friction stir welds (FSWs), producing fine and uniform equiaxed grains. In this study, partial dynamic recrystallization was observed in the NZ of 5 mm thick friction stir welded brass plates. Whereas the top and the advancing side of the NZ were characterized by fine completely-recrystallized grains, the remaining region consisted of coarse non-recrystallized deformed grains, annealed recrystallized grains and deformed recrystallized grains. The occurrence of partial recrystallization was attributed to the inhibiting effect of a high volume fraction of fine beta'-phase particles. Increasing the FSW passes reduced the fraction and size of non-recrystallized deformed grains, but could not eliminate the partially recrystallized zone completely. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32446]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | G. M. Xie,Z. Y. Ma,L. Geng. Partial recrystallization in the nugget zone of friction stir welded dual-phase Cu-Zn alloy[J]. Philosophical Magazine,2009,89(18):1505-1516. |
| APA | G. M. Xie,Z. Y. Ma,&L. Geng.(2009).Partial recrystallization in the nugget zone of friction stir welded dual-phase Cu-Zn alloy.Philosophical Magazine,89(18),1505-1516. |
| MLA | G. M. Xie,et al."Partial recrystallization in the nugget zone of friction stir welded dual-phase Cu-Zn alloy".Philosophical Magazine 89.18(2009):1505-1516. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。