Phosphating treatment and corrosion properties of Mg-Mn-Zn alloy for biomedical application
文献类型：期刊论文
| 作者 | L. P. Xu ; E. L. Zhang ; K. Yang |
| 刊名 | Journal of Materials Science-Materials in Medicine
 |
| 出版日期 | 2009 |
| 卷号 | 20期号:4页码:859-867 |
| 关键词 | in-vivo corrosion az31 magnesium alloy calcium phosphates coatings brushite hydroxyapatite behavior cements zinc protection |
| ISSN号 | 0957-4530 |
| 中文摘要 | A phosphating treatment was applied to Mg-Mn-Zn alloy in order to improve the corrosion resistance. Surface morphology and phase constitute were observed and identified by SEM, EDS, SAXS, XRD and XPS. SEM observation showed that a rough and crystalline reaction layer was formed on the surface of Mg alloy. With the increasing of phosphating time, the layer became thicker and denser. It has been showed that the reaction layer was mainly composed of brushite (CaHPO(4) center dot A 2H(2)O). Small amount of Zn(2+) was also detected by XPS and EDS. The corrosion resistance of the phosphated samples was measured by the electrochemical polarization and the immersion test in comparison with the bare alloy. The results manifested that the corrosion resistance of Mg alloy was improved by the phosphating treatment, and the corrosion resistance increased with the increase of the phosphating time within 50 min. Immersion tests showed that the phosphate layer could protect magnesium alloy from fast corrosion. The brushite layer has been transformed into hydroxyapatite (HA) during the immersion in the simulated body fluid (SBF) solution, which suggested the brushite layer could provide good biocompatibility. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32460]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. P. Xu,E. L. Zhang,K. Yang. Phosphating treatment and corrosion properties of Mg-Mn-Zn alloy for biomedical application[J]. Journal of Materials Science-Materials in Medicine,2009,20(4):859-867. |
| APA | L. P. Xu,E. L. Zhang,&K. Yang.(2009).Phosphating treatment and corrosion properties of Mg-Mn-Zn alloy for biomedical application.Journal of Materials Science-Materials in Medicine,20(4),859-867. |
| MLA | L. P. Xu,et al."Phosphating treatment and corrosion properties of Mg-Mn-Zn alloy for biomedical application".Journal of Materials Science-Materials in Medicine 20.4(2009):859-867. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。