Synthesis of YAG powder by the modified sol-gel combustion method
文献类型：期刊论文
| 作者 | L. Yang ; T. C. Lu ; H. Xu ; N. A. Wei |
| 刊名 | Journal of Alloys and Compounds
 |
| 出版日期 | 2009 |
| 卷号 | 484期号:1-2页码:449-451 |
| 关键词 | Nanostructured materials Sol-gel processes X-ray diffraction Thermal analysis yttrium-aluminum-garnet luminescence properties ceramics phosphor laser nanoparticles performance fabrication precursors water |
| ISSN号 | 0925-8388 |
| 中文摘要 | Yttrium aluminum garnet (YAG) precursor was prepared by sol-gel combustion method using ethanol as solvent. Nano-sized YAG powders were obtained by precalcining the precursor at 500 degrees C, and then calcining at different temperatures. The phase formation and characteristics of YAG powders were investigated by means of XRD, TG/DSC and TEM. Pure crystalline YAG phase was obtained at 800 degrees C, without any intermediate phases such as YAlO(3) (YAP) and Y(4)Al(2)O(9) (YAM). Moreover, it was found that the elliptical YAG powder calcined at 900 degrees C for 2 h was well-crystallized with an average size of 30 nm, and had a good dispersity. (C) 2009 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32490]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Yang,T. C. Lu,H. Xu,et al. Synthesis of YAG powder by the modified sol-gel combustion method[J]. Journal of Alloys and Compounds,2009,484(1-2):449-451. |
| APA | L. Yang,T. C. Lu,H. Xu,&N. A. Wei.(2009).Synthesis of YAG powder by the modified sol-gel combustion method.Journal of Alloys and Compounds,484(1-2),449-451. |
| MLA | L. Yang,et al."Synthesis of YAG powder by the modified sol-gel combustion method".Journal of Alloys and Compounds 484.1-2(2009):449-451. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。