Biocorrosion behavior of magnesium alloy in different simulated fluids for biomedical application
文献类型：期刊论文
| 作者 | L. Yang ; E. L. Zhang |
| 刊名 | Materials Science & Engineering C-Biomimetic and Supramolecular Systems
 |
| 出版日期 | 2009 |
| 卷号 | 29期号:5页码:1691-1696 |
| 关键词 | Magnesium alloy Biomaterials Simulated solution Corrosion in-vivo corrosion body-fluid mechanical-properties mg bone microstructure degradation vitro si |
| ISSN号 | 0928-4931 |
| 中文摘要 | The biocorrosion behavior of a magnesium alloy in two simulated body solutions, Hank's Solution and simulated blood plasma (SBP) solution was investigated by electrochemical and weight loss testing for biomedical application. The solution volume/surface area (SV/SA) ratio was changed to reveal the effect of immersion condition on the biocorrosion behavior. A same tendency was observed in the corrosion rate of magnesium alloy in all testing conditions: a high corrosion rate at the initial stage, and rapid decrease in the first 2-3 days followed by a stable corrosion rate in the following stage. A higher corrosion rate was observed in Hank's solution than in SBP solution due to high Cl(-), low Ca(2+) and PO(4)(3-) concentration in Hank's solution. However, no difference in the surface reaction product was observed between the samples immersed in Hank's solution and in SBP solution. It was found that the SV/SA ratio significantly affected the corrosion rate of magnesium alloy. Low ratio resulted ill a high pH, which resisted the corrosion. But When the ratio was high enough, 6.7 for example, the influence was negligible. By changing the ratio, the biocorrosion behavior of magnesium implant in different implantation sites can be simulated, for example, low ratio for the case of in muscle and high ratio for the case of in marrow cavity. It is suggested that selection of the simulated solution and the SV/SA ratio would be very necessary to Simulate different the in-vivo biodegradation behavior of magnesium in different implantation environment. (C) 2009 Elsevier B.V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32491]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | L. Yang,E. L. Zhang. Biocorrosion behavior of magnesium alloy in different simulated fluids for biomedical application[J]. Materials Science & Engineering C-Biomimetic and Supramolecular Systems,2009,29(5):1691-1696. |
| APA | L. Yang,&E. L. Zhang.(2009).Biocorrosion behavior of magnesium alloy in different simulated fluids for biomedical application.Materials Science & Engineering C-Biomimetic and Supramolecular Systems,29(5),1691-1696. |
| MLA | L. Yang,et al."Biocorrosion behavior of magnesium alloy in different simulated fluids for biomedical application".Materials Science & Engineering C-Biomimetic and Supramolecular Systems 29.5(2009):1691-1696. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。