Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction
文献类型：期刊论文
| 作者 | K. Yin ; W. M. Ma ; L. Wen ; S. F. Shen ; H. D. Wang ; Y. F. Guo |
| 刊名 | Chinese Journal of Inorganic Chemistry
 |
| 出版日期 | 2009 |
| 卷号 | 25期号:7页码:1248-1253 |
| 关键词 | scintillant BaHfO(3):Ce nanoparticles solid-state reaction process excitation spectrum emission spectrum combustion synthesis photoluminescence phosphors y2o3-eu ca sr ba nanophosphors fabrication ceramics |
| ISSN号 | 1001-4861 |
| 中文摘要 | BaHfO(3):Ce nanoparticles were synthesized by the process of solid-state reaction. Both XRD and SEM were adopted to analyze the phase change and the characteristics of BaHfO(3):Ce nano-powders during calcining process. Excitation and emission spectra were analyzed separately with the fluorescence photometer. The result shows that the average diameter of the BaHfO(3):Ce nano-powders being approximate to spherical morphology is about 30 nm and the powders have good dispersibility after calcining at 1000 degrees C for 2 h. It also shows that there is no change happened on the cubic crystal structure even though a little amount of Ce(3+) ion added to the powders can lead to the lattice distortion of BaHfO(3) matrix material. The excitation spectrum of BaHfO(3): Ce nanoparticles has two excitation peaks separately at 396 nm and 446 nm points. The emission spectrum excited by the 396 nm light consists of two emission bands, peaking at 531 nm and 591 run, respectively, the emission character of which changes from the 5d ->(2)F(5/2) to 5d ->(2)F(7/2) transitions of Ce(3+) cation. When the emission spectrum is excited by the 446 nm light, only one wide emission peak at 591 nm point exists and the other one at around 531 nm becomes flat. When the Ce(3+) dopant content is 0.9%(molar fraction), the figure of the emission peak reaches its highest point. This figure, however, drops when The Ce(3+) dopant content is 1.1%( molar fraction), which is resulted from the concentraction quenching. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32506]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | K. Yin,W. M. Ma,L. Wen,et al. Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction[J]. Chinese Journal of Inorganic Chemistry,2009,25(7):1248-1253. |
| APA | K. Yin,W. M. Ma,L. Wen,S. F. Shen,H. D. Wang,&Y. F. Guo.(2009).Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction.Chinese Journal of Inorganic Chemistry,25(7),1248-1253. |
| MLA | K. Yin,et al."Preparation and Luminescence Characteristics of BaHfO(3):Ce Nanoparticles by the Process of Solid-State Reaction".Chinese Journal of Inorganic Chemistry 25.7(2009):1248-1253. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。