Direct diffusion bonding of Ti(3)SiC(2) and Ti(3)AlC(2)

文献类型:期刊论文

作者X. H. Yin ; M. S. Li ; J. J. Xu ; J. Zhang ; Y. C. Zhou
刊名Materials Research Bulletin
出版日期2009
卷号44期号:6页码:1379-1384
关键词Carbids Layered compounds Diffusion Microstructure liquid reaction synthesis ti3al1-xsixc2 solid-solutions mechanical strength oxidation behavior microstructure ceramics si interlayer carbide joints
ISSN号0025-5408
中文摘要Two typical layered ternary compounds. Ti(3)SiC(2) and Ti(3)AlC(2), were joined directly by solid-state diffusion bonding method. By various bonding tests at 1100-1300 degrees C for 30-120 min under 10-30 MPa, and characterizing the microstructure and diffusion reactive phases of the joints by scanning electron microscopy (SEM). energy dispersive X-ray spectrometer (EDS), transmission electron microscopy (TEM) and X-ray diffraction (XRD). the optimal condition for direct joining of Ti(3)SiC(2) and Ti(3)AlC(2) was obtained. Strong joints of Ti(3)SiC(2)/Ti(3)AlC(2) can be achieved via diffusion bonding, which is attributed to remarkable interdiffusion of Si and Al at the joint interface. The shear strength of the Ti(3)SiC(2)/Ti(3)AlC(2) joints was determined. (C) 2008 Elsevier Ltd. All rights reserved.
原文出处://WOS:000265906600032
公开日期2012-04-13
源URL[http://210.72.142.130/handle/321006/32507]  
专题金属研究所_中国科学院金属研究所
推荐引用方式
GB/T 7714
X. H. Yin,M. S. Li,J. J. Xu,et al. Direct diffusion bonding of Ti(3)SiC(2) and Ti(3)AlC(2)[J]. Materials Research Bulletin,2009,44(6):1379-1384.
APA X. H. Yin,M. S. Li,J. J. Xu,J. Zhang,&Y. C. Zhou.(2009).Direct diffusion bonding of Ti(3)SiC(2) and Ti(3)AlC(2).Materials Research Bulletin,44(6),1379-1384.
MLA X. H. Yin,et al."Direct diffusion bonding of Ti(3)SiC(2) and Ti(3)AlC(2)".Materials Research Bulletin 44.6(2009):1379-1384.

入库方式: OAI收割

来源:金属研究所

浏览0
下载0
收藏0
其他版本

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。