Cavitation Erosion Corrosion Behaviour of Manganese-nickel-aluminum Bronze in Comparison with Manganese-brass
文献类型：期刊论文
| 作者 | H. Yu ; Y. G. Zheng ; Z. M. Yao |
| 刊名 | Journal of Materials Science & Technology
 |
| 出版日期 | 2009 |
| 卷号 | 25期号:6页码:758-766 |
| 关键词 | Cavitation erosion Marine propeller Manganese-nickel-aluminum bronze Manganese-brass Synergism Work-hardening ability Stacking fault energy stacking-fault energy alloy seawater steels cast |
| ISSN号 | 1005-0302 |
| 中文摘要 | The cavitation erosion corrosion behaviour of ZQMn12-8-3-2 manganese-nickel-aluminum bronze and ZHMn55-3-1 manganese-brass was investigated by mass loss, electrochemical measurements (polarization curves and electrochemical impedance spectroscopy) and the cavitation damaged surfaces were observed by scanning electron microscopy (SEM). The results showed that ZQMn12-8-3-2 had better cavitation erosion resistance than ZHMn55-3-1. After the cavitation erosion for 6 h, the cumulative mass loss of ZQMn12-8-3-2 was about 1/3 that of ZHMn55-3-1. The corrosion current density of ZQMn12-8-3-2 was less than that of ZHMn55-3-1 under both static and cavitaiton condition. The free-corrosion potentials of ZQMn12-8-3-2 and ZHMn55-3-1 were all shifted in positive direction under cavitation condition compared to static condition. In the total cumulative mass loss under cavitation condition, the pure erosion played a key role for the two tested materials (74% for ZHMn55-3-1 and 60% for ZQMn12-8-3-2), and the total synergism between corrosion and erosion of ZQMn12-8-3-2 (39%) was larger than that of ZHMn55-3-1 (23%). The high cavitation erosion resistance of ZQMn12-8-3-2 was mainly attributed to its lower stacking fault energy (SFE), the higher microhardness and work-hardening ability as well as the favorable propagation of cavitation. cracks for ZQMn12-8-3-2, i.e., parallel to the surface rather than perpendicular to the surface for ZHMn55-3-1. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32511]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. Yu,Y. G. Zheng,Z. M. Yao. Cavitation Erosion Corrosion Behaviour of Manganese-nickel-aluminum Bronze in Comparison with Manganese-brass[J]. Journal of Materials Science & Technology,2009,25(6):758-766. |
| APA | H. Yu,Y. G. Zheng,&Z. M. Yao.(2009).Cavitation Erosion Corrosion Behaviour of Manganese-nickel-aluminum Bronze in Comparison with Manganese-brass.Journal of Materials Science & Technology,25(6),758-766. |
| MLA | H. Yu,et al."Cavitation Erosion Corrosion Behaviour of Manganese-nickel-aluminum Bronze in Comparison with Manganese-brass".Journal of Materials Science & Technology 25.6(2009):758-766. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。