Synthesis and characteristics of 80 vol.% tungsten (W) fibre/Zr based metallic glass composite
文献类型：期刊论文
| 作者 | H. F. Zhang ; H. Li ; A. M. Wang ; H. M. Fu ; B. Z. Ding ; Z. Q. Hu |
| 刊名 | Intermetallics
 |
| 出版日期 | 2009 |
| 卷号 | 17期号:12页码:1070-1077 |
| 关键词 | Glasses metallic Bonding Composites based on the metallic glass matrix Mechanical testing matrix composites mechanical-properties fracture-behavior dynamic deformation shear bands bulk phase plasticity interface property |
| ISSN号 | 0966-9795 |
| 中文摘要 | Based on full understanding of wettability between Zr based bulk metallic glass (BMG) matrix and tungsten (W) fibre, and liquid/solid interfacial atomic interaction, the high density and high strength 80 vol.% W fibre/Zr based BMG composite, with optimum interfacial layer, was successfully developed by strictly controlling the infiltration and solidification process. Its density was 17 g/cm(3). The average value of tensile fracture strength was 1685 MPa. Fracture mode represented instant rupture which was vertical to the axial direction. The average value of compressive fracture strength and strain were 2550 MPa and 23% respectively. Its fracture mode was complex splitting along loading direction. The initiation of shear bands occurred when the compressive specimen reached plastic strength. Shear bands' continuous expanding, branching, propagation and build up responded the improvement of plasticity under the continuous loading. Shear bands distributed on the fracture surface in two ways. One was consistent with the maximum shear force direction and at 45 degrees angle with the loading direction. The other was nearly horizontal and vertical to the loading direction. The characteristics of plastic deformation and fracture were also investigated and discussed in detail. (C) 2009 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32540]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | H. F. Zhang,H. Li,A. M. Wang,et al. Synthesis and characteristics of 80 vol.% tungsten (W) fibre/Zr based metallic glass composite[J]. Intermetallics,2009,17(12):1070-1077. |
| APA | H. F. Zhang,H. Li,A. M. Wang,H. M. Fu,B. Z. Ding,&Z. Q. Hu.(2009).Synthesis and characteristics of 80 vol.% tungsten (W) fibre/Zr based metallic glass composite.Intermetallics,17(12),1070-1077. |
| MLA | H. F. Zhang,et al."Synthesis and characteristics of 80 vol.% tungsten (W) fibre/Zr based metallic glass composite".Intermetallics 17.12(2009):1070-1077. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。