Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts
文献类型：期刊论文
| 作者 | J. F. Zhang ; C. W. Yan ; F. H. Wang |
| 刊名 | Applied Surface Science
 |
| 出版日期 | 2009 |
| 卷号 | 255期号:9页码:4926-4932 |
| 关键词 | Magnesium alloy Electrodeposition Al-Mn alloy Zn intermediate layer Corrosion resistance sodium chloride bath corrosion-resistance aluminum improvement deposition powder melts |
| ISSN号 | 0169-4332 |
| 中文摘要 | The Al-Mn alloy coatings were electrodeposited on AZ31B Mg alloy in AlCl(3)-NaCl-KCl-MnCl(2) molten salts at 170 degrees C aiming to improve the corrosion resistance. However, in order to prevent AZ31B Mg alloy from corrosion during electrodeposition in molten salts and to ensure excellent adhesion of coatings to the substrate, AZ31B Mg alloy should be pre-plated with a thin zinc layer as intermediate layer. Then the microstructure, composition and phase constituents of the coatings were investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDX), and X-ray diffraction (XRD). It was indicated that, by adjusting the MnCl(2) content in the molten salts from 0.5 wt% to 2 wt%, the Mn content in the alloy coating was increased and the phase constituents were changed from f.c.c Al-Mn solid solution to amorphous phase. The corrosion resistance of the coatings was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was confirmed that the Al-Mn alloy coatings exhibited good corrosion resistance with a chear passive region and significantly reduced corrosion current density at anodic potentiodynamic polarization. The corrosion resistance of the alloy coatings was also related with the microstructure and Mn content of the coatings. (C) 2009 Elsevier B. V. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32550]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | J. F. Zhang,C. W. Yan,F. H. Wang. Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts[J]. Applied Surface Science,2009,255(9):4926-4932. |
| APA | J. F. Zhang,C. W. Yan,&F. H. Wang.(2009).Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts.Applied Surface Science,255(9),4926-4932. |
| MLA | J. F. Zhang,et al."Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts".Applied Surface Science 255.9(2009):4926-4932. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。