Carbon-coated Li3V2(PO4)(3) composite cathode material for lithium-ion batteries: Sol-gel synthesis and performance
文献类型：期刊论文
| 作者 | Q. Q. Chen ; W. C. He ; J. M. Wang ; Z. Tang ; H. B. Shao ; J. Q. Mang |
| 刊名 | Chinese Journal of Inorganic Chemistry
 |
| 出版日期 | 2008 |
| 卷号 | 24期号:2页码:181-190 |
| 关键词 | Li3V2(PO4)(3) sol-gel method carbon-coated lithium-ion batteries state synthesis routine electrochemical performance high-capacity lifepo4 pyrolysis precursor surface xps fe |
| ISSN号 | 1001-4861 |
| 中文摘要 | A carbon-coated Li3V2(PO4)(3) Composite cathode material was synthesized by a sol-gel method using V2O5, LIOH center dot H2O, H2O2, NH4H2PO4 and citric acid as starting materials. Properties of the prepared composite material were investigated using XPS, XRD, SEM, Raman spectroscopy, TEM, and various electrochemical techniques. The relationship among structure, calcination temperature, electronic conductivity and the electrochemical performance of samples was also studied. The sample obtained had a monoclinic structure with a space group of P2(1)/n and a rough and porous carbon surface layer. The electronic conductivity of the carbon-coated Li3V2(PO4)3 samples synthesized at 800 degrees C was about a factor of similar to 10(4) higher than that of carbon-free Li3V2(PO4)(3) prepared by solid-state hydrogen reducing reaction. The results show that the carbon-coated Li3V2(PO4)(3) is superior in the electrochemical performance to the carbon-free sample. In the voltage range of 3.0 similar to 4.3 V, the carbon-coated Li3V2(PO4)(3) synthesized at 800 degrees C displays large reversible capacities (128 mAh center dot g(-1) at 0.1C and 109 mAh center dot g(-1) at 2C, respectively) and excellent cyclic stability. The reason for the excellent electrochemical performance of the carbon coated Li3V2(PO4)(3) is discussed. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32676]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Q. Q. Chen,W. C. He,J. M. Wang,et al. Carbon-coated Li3V2(PO4)(3) composite cathode material for lithium-ion batteries: Sol-gel synthesis and performance[J]. Chinese Journal of Inorganic Chemistry,2008,24(2):181-190. |
| APA | Q. Q. Chen,W. C. He,J. M. Wang,Z. Tang,H. B. Shao,&J. Q. Mang.(2008).Carbon-coated Li3V2(PO4)(3) composite cathode material for lithium-ion batteries: Sol-gel synthesis and performance.Chinese Journal of Inorganic Chemistry,24(2),181-190. |
| MLA | Q. Q. Chen,et al."Carbon-coated Li3V2(PO4)(3) composite cathode material for lithium-ion batteries: Sol-gel synthesis and performance".Chinese Journal of Inorganic Chemistry 24.2(2008):181-190. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。