Enhancement of corrosion performance of epoxy coatings by chemical modification with GPTMS silane monomer
文献类型：期刊论文
| 作者 | W. G. Ji ; J. M. Hu ; L. Liu ; J. Q. Zhang ; C. N. Cao |
| 刊名 | Journal of Adhesion Science and Technology
 |
| 出版日期 | 2008 |
| 卷号 | 22期号:1页码:77-92 |
| 关键词 | epoxy coatings 3-glycidoxypropyltrimethoxysilane (GPTMS) chemical modification corrosion performance electrochemical impedance spectroscopy metal pretreatments coated metals aa 2024-t3 aluminum protection steel films degradation resistance |
| ISSN号 | 0169-4243 |
| 中文摘要 | In this paper, commercial epoxy resin was chemically modified by different amounts of 3-glycidoxypropyltrimethoxysilane (GPTMS) monomer using an organotin compound as catalyst, aiming to improve the anti-corrosion performance of epoxy coatings on 2024-T3 aluminum alloy substrate. Electrochemical impedance spectroscopy (EIS) was used to evaluate the barrier properties against water permeation and protectiveness of silane-modified epoxy coatings. The results showed that all the modified coatings presented higher barrier performance and better corrosion perfon-nance than pure epoxy coating, which were characterized by higher charge transfer resistance (R-ct) and lower double-layer capacitance (C-dl) at the electrolyte/metal interface. The improvements in corrosion performance and wet adhesion of modified epoxy coatings were also observed by the Machu test and boiling water test, respectively. Interestingly, it was found that the glass-transition temperature (T-g) of silane-modified epoxy coatings decreased only slightly during immersion in 3.5 wt% NaCl solution, in contrast with pure epoxy coating, which was observed to decrease significantly after water permeation. The corrosion performance of epoxy coatings was, thus, improved when the amount of chemically grafted silane monomer increased in the content range investigated in the present work. (c) Koninklijke Brill NV, Leiden, 2008. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://ir.imr.ac.cn/handle/321006/32842]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | W. G. Ji,J. M. Hu,L. Liu,et al. Enhancement of corrosion performance of epoxy coatings by chemical modification with GPTMS silane monomer[J]. Journal of Adhesion Science and Technology,2008,22(1):77-92. |
| APA | W. G. Ji,J. M. Hu,L. Liu,J. Q. Zhang,&C. N. Cao.(2008).Enhancement of corrosion performance of epoxy coatings by chemical modification with GPTMS silane monomer.Journal of Adhesion Science and Technology,22(1),77-92. |
| MLA | W. G. Ji,et al."Enhancement of corrosion performance of epoxy coatings by chemical modification with GPTMS silane monomer".Journal of Adhesion Science and Technology 22.1(2008):77-92. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。