Optimization of heat treatment in AZ64 magnesium alloy
文献类型：期刊论文
| 作者 | S. Liang ; Y. Ma ; R. Chen ; E. Han |
| 刊名 | Materials Transactions
 |
| 出版日期 | 2008 |
| 卷号 | 49期号:5页码:986-989 |
| 关键词 | AZ64 magnesium alloy thermal analysis two-step solution treatment mechanical properties ductility strength |
| ISSN号 | 1345-9678 |
| 中文摘要 | The heat treatment parameters of AZ64 magnesium alloy have been optimized using thermal analysis, scanning electron microscopy and X-ray diffraction techniques. The thermal analysis result revealed that two precipitation reactions took place during the solidification of AZ64 alloy. Therefore, a two-step solution heat treatment method, instead of traditional solution treatment whose temperature was about 10 degrees C below the solidus temperature, was developed corresponding to the dissolution of two precipitate phases. With comparison to the traditional heat treatment, the two-step treatment method could generate a complete solution effect. During the following aging process, precipitates almost uniformly dispersed throughout the matrix, thus improve the tensile strength of alloy. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/32918]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | S. Liang,Y. Ma,R. Chen,et al. Optimization of heat treatment in AZ64 magnesium alloy[J]. Materials Transactions,2008,49(5):986-989. |
| APA | S. Liang,Y. Ma,R. Chen,&E. Han.(2008).Optimization of heat treatment in AZ64 magnesium alloy.Materials Transactions,49(5),986-989. |
| MLA | S. Liang,et al."Optimization of heat treatment in AZ64 magnesium alloy".Materials Transactions 49.5(2008):986-989. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。