Oxidation at 900 degrees C of the chromized coatings on A3 carbon steel with the electrodeposition pretreatment of Ni or Ni-CeO(2) film
文献类型：期刊论文
| 作者 | X. Peng ; J. Yan ; C. Xu ; F. Wang |
| 刊名 | Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science
 |
| 出版日期 | 2008 |
| 卷号 | 39A期号:1页码:119-129 |
| 关键词 | nickel alloys diffusion behavior growth microstructures delamination resistance platinum |
| ISSN号 | 1073-5623 |
| 中文摘要 | Chromized coatings developed on a mild carbon steel (A3) using a conventional halide-activated pack cementation method at 1120 degrees C inevitably formed chromium carbides in the surface zone, which is the crucial factor giving the coatings a fast scaling rate in 5 pct O(2) + N(2) at 900 degrees C, and simultaneously a severe scale spallation during cooling. No chromium carbides were seen in the chromized coatings, when the steel was pretreated with a similar to 80-mu m-thick precursor film of electrodeposited Ni Without or with dispersions of similar to 5.5 wt pct CeO(2) nanoparticles. However, during oxidation of the chromized, Ni-film-treated coating in 5 pet O(2) + N(2), fresh chromium carbides were intensively precipitated in the Coating near-surface zone. The carbides' oxidation caused the formation of the scale, with an increased susceptibility to cracking and spalling. For the chromized, Ni-CeO(2)-nanocomposite-treated A3, chromium carbides were sporadically precipitated throughout the entire coating during oxidation, and the negative effect of the carbides on oxidation was prevented. This, together with the reactive element effect (REE) of the added CeO(2) during oxidation, is proposed for this coating, for the purpose of thermally forming a chromia scale with a noticeably reduced growth rate and also an enhanced adhesion. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33047]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | X. Peng,J. Yan,C. Xu,et al. Oxidation at 900 degrees C of the chromized coatings on A3 carbon steel with the electrodeposition pretreatment of Ni or Ni-CeO(2) film[J]. Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,2008,39A(1):119-129. |
| APA | X. Peng,J. Yan,C. Xu,&F. Wang.(2008).Oxidation at 900 degrees C of the chromized coatings on A3 carbon steel with the electrodeposition pretreatment of Ni or Ni-CeO(2) film.Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science,39A(1),119-129. |
| MLA | X. Peng,et al."Oxidation at 900 degrees C of the chromized coatings on A3 carbon steel with the electrodeposition pretreatment of Ni or Ni-CeO(2) film".Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science 39A.1(2008):119-129. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。