Hot corrosion Of gamma-Y2Si2O7 in strongly basic Na2CO3 molten salt environment
文献类型：期刊论文
| 作者 | Z. Q. Sun ; M. S. Li ; Z. P. Li ; Y. C. Zhou |
| 刊名 | Journal of the European Ceramic Society
 |
| 出版日期 | 2008 |
| 卷号 | 28期号:1页码:259-265 |
| 关键词 | Y2Si2O7 corrosion silicates structural applications engine components yttrium silicate coatings oxidation protection alkali corrosion si3n4 ceramics nitride composites na2so4 solubility disilicate mechanism |
| ISSN号 | 0955-2219 |
| 中文摘要 | gamma-Y2Si2O7 is a promising candidate both for high temperature structural applications and as thermal barrier coatings due to its unique combination of properties, such as high melting point, good machinability, high thermal stability, low linear thermal expansion coefficient (3.9 x 10(-6) K-1, 25-1400 degrees C) and low thermal conductivity (< 3 W/m K above 300 degrees C). In this work, the hot corrosion behavior of gamma-Y2Si2O7 in strongly basic Na2CO3 molten salt at 850-1000 degrees C for 20 h in flowing air was investigated. In the employed conditions, multi-layer corrosion scales with total thickness less than 90 mu m were formed. At 850-900 degrees C, the outmost layer of the scale was composed of the reprecipitation Of Y2O3, the bottom of a Si-rich Na2O center dot xSiO(2) (x > 3.65) melt layer, and the middle of a NaYSiO4 layer. At 1000 degrees C, the corrosion products turned out to be a mixture of NaY9Si6O26 and Si-rich Na2O center dot xSiO(2) (x > 3.65). In all cases, a thin layer of protective SiO2 formed under the Na2O center dot XSiO2 melt and protected the bulk material from further corrosion. (c) 2007 Elsevier Ltd. All rights reserved. |
| 原文出处 | |
| 公开日期 | 2012-04-13 |
| 源URL | [http://210.72.142.130/handle/321006/33092]  |
| 专题 | 金属研究所_中国科学院金属研究所 |
| 推荐引用方式 GB/T 7714 | Z. Q. Sun,M. S. Li,Z. P. Li,et al. Hot corrosion Of gamma-Y2Si2O7 in strongly basic Na2CO3 molten salt environment[J]. Journal of the European Ceramic Society,2008,28(1):259-265. |
| APA | Z. Q. Sun,M. S. Li,Z. P. Li,&Y. C. Zhou.(2008).Hot corrosion Of gamma-Y2Si2O7 in strongly basic Na2CO3 molten salt environment.Journal of the European Ceramic Society,28(1),259-265. |
| MLA | Z. Q. Sun,et al."Hot corrosion Of gamma-Y2Si2O7 in strongly basic Na2CO3 molten salt environment".Journal of the European Ceramic Society 28.1(2008):259-265. |
入库方式： OAI收割
来源：金属研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。